Method for producing a collapse resistant polyester container for hot fill applications
AssigneeMonsanto Company
InventorsPurushottam D. Agrawal, John F. Mandell
Life of this patent
Estimating the term…
Abstract
A collapse resistant polyester container is provided for hot fill applications employing product fill temperatures up to about 190.degree. F. (87.8.degree. C.) or more. The container has at least one region which is thermoelastically deformable inwardly after the container is hot filled and sealed to offset the pressure forces which tend to collapse the container as the contents cool and create an internal vacuum. The thermoelastic region is preferably formed in a two step molding process in which the region is formed and heat set at a first position and then reformed outwardly to a second position and cooled in that position.
Claims20
A method for producing a collapse resistant, molecularly oriented, heat set polyester container for use in hot fill applications, said method comprising the steps of:
- (a) forming in a mold cavity a molecularly oriented polyester container having at least one preselected region which projects inwardly into said container in a first configuration;
- (b) heating said oriented container while in contact with the cavity walls at a temperature sufficient to induce rapid crystallization of the polyester to form a heat set container, at least said region being heated to a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said region;
- (c) reshaping said region outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the heating temperature of step (b);
- and
- (d) cooling the resulting container while maintaining said region in said second configuration to provide a thermoelastically deformable region which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.
A method for producing a collapse resistant, molecularly oriented, heat set polyester container for use in hot fill applications, said method comprising the steps of
- (a) distending a substantially amorphous polyester preform at a temperature within the molecular orientation temperature range of said polyester in a mold to form an oriented container having sidewalls and a base, said base being formed in a first configuration which projects inwardly into said container;
- (b) heating said oriented container in and while in contact with walls of said mold, at a temperature sufficient to induce rapid crystallization of said polyester to form a heat set container, at least the inwardly projecting base being heated to a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said base;
- (c) reshaping said base outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the heating temperature of step (b);
- and
- (d) cooling the resulting container while maintaining said base in said second configuration to provide a thermoelastically deformable base which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.
A method for producing a collapse resistant, oriented heat set polyester container for use in hot fill applications, said method comprising the steps of:
- (a) distending a substantially amorphous polyester preform at a temperature in the molecular orientation temperature range of said polyester in a mold to form an oriented container having sidewalls and a base, said base being formed in a first configuration which projects inwardly into said container;
- (b) differentially heating said oriented container in and while in contact with walls of said mold, said differential heating comprising heating said sidewalls at a temperature and for a time sufficient to produce at least about 35% crystallinity in said sidewalls, and heating said base at a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said base;
- (c) reshaping said base outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the base heating temperature of step (b);
- and
- (d) cooling the resulting container while maintaining said base in said second configuration to provide a thermoelastically deformable base which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.