Two stage procedure for the preparation of polypyrrolidone
AssigneeStamicarbon B.V.
InventorsEdmond H. J. P. Bour, Johannes A. L. Brouwers, Jean M. M. Warnier
Life of this patent
Estimating the term…
Abstract
Polypyrrolidone polymers and copolymers are obtained by polymerizing 2-pyrrolidone, optionally with another lactam, in the presence of a catalyst and accelerator, first in the mass until at least 10% of the monomer is converted but the reaction product is still capable of suspension, then completing the desired degree of polymerization by suspending the reaction mixture in an inert liquid dispersion agent that does not dissolve the desired polymer. Relatively high molecular weight polymers are prepared in a short amount of time using this two-stage procedure.
Claims6
In a process for preparing a solid, particulate polymer from a 2-pyrrolidone monomer composition comprising 2-pyrrolidone and 0-25 mol %, based on 2-pyrrolidone, of a different copolymerizable lactam, with at least one polymerization catalyst and at least one polymerization accelerator,
- the improvement comprising polymerizing said monomer composition in two distinct stages, wherein:
- (1) in a first stage, 2-pyrrolidone monomer composition is polymerized in the mass whereby, apart from the reactants, not more than roughly 15 volume %, based on the volume of the reactants, of a liquid dispersion agent or other liquid is present, for a period of between 5 minutes and 4 hours until the conversion of the monomer composition is at least 10% to form a reaction mass which is capable of being suspended in a liquid, and thereafter,
- (2) in a second stage, suspending the reaction mass in an inert liquid dispersing agent in which the polymer of 2-pyrrolidone is insoluble, and continuing the polymerization of the reaction mass until the particulate polymer is formed.