Lump process alpha gypsum
AssigneeUnited States Gypsum Company
InventorEugene O'Neill
Life of this patent
Estimating the term…
Abstract
An improved "lump" process for producing alpha gypsum, calcium sulfate hemihydrate, from natural gypsum rock of the type wherein lumps of gypsum rock particles (a minimum of about 1/2 inch or 1.3 cm. in size) are calcined to low water-demand alpha hemihydrate by autoclaving in a saturated steam atmosphere, quickly dried and pulverized is disclosed. The improvement allows the thorough processing of natural gypsum as large sized particles or containing considerable selenite and includes the steps of initiating calcination without crystal habit modifier and, after hemihydrate formation has commenced, adding crystal habit modifier and completing calcination under increased steam pressure.
Claims6
In a process for the production of alpha calcium sulfate hemihydrate crystals of the type wherein lump gypsum particles of at least about 1/2 inch size are calcined at steam pressures of 13 to 60 psi gauge in a state of quiescence and with an at least first lower pressure cycle and a second higher pressure cycle, dried and ground to obtain calcium sulfate hemihydrate having a low normal consistency, the improvement comprising:
- heating under the lower pressure cycle without a crystal habit modifier to convert at least a substantial but minor part of the gypsum to hemihydrate;
- intermediate the low pressure and high pressure cycles adding an aqueous solution of crystal-habit-modifier;
- and
- continuing calcination under steam pressure until substantially all of the gypsum particles are converted to hemihydrate crystals.
In a process for producing alpha calcium sulfate hemihydrate crystals of the type wherein lump gypsum particles of at least about 1/2 inch size are calcined under steam pressures of 13 to 60 psi gauge in a state of quiescence and with a first lower pressure cycle with an aqueous solution of crystal-habit-modifier and a second higher pressure cycle, drying and grinding the product to obtain calcium sulfate hemihydrate having low normal consistency, the improvement of adding crystal-habit modifier solution in a plurality of discontinuous portions comprising:
- applying a first portion of the crystal-habit-modifier solution to the surface of the gypsum particles before autoclave calcination;
- and
- intermediate the lower pressure and higher pressure cycles adding in at least one second distinct portion, the remainder of the crystal-habit-modifier solution;
- and
- continuing calcination under steam pressure until substantially all of the gypsum particles are converted to hemihydrate crystals.
Dependencies are inferred from the claim text.