Low density compacts of prepared mix for use in the production of silicon and ferrosilicon

A method of making low density, porous compacts for use in the production of silicon and ferrosilicon comprising blending together a finely-divided silica-containing material including at least about 25 parts by weight of silica fume per 100 parts by weight of total silica, a finely-divided carbonaceous reducing agent in an amount such that the total carbon ranges from about 35 to 50 parts by weight carbon per 100 parts by weight of total silica, and from about 0 to about 15 parts by weight of iron particles, about 2.5 parts by weight of a cereal binder and about 50 parts by weight water per 100 parts by weight of total silica, to form a wet mix, said silica fume having a particle size of less than about 0.5 microns;

• depositing the wet mix evenly in a relatively thin layer over a flat surface, drying the mix at elevated temperatures in order to remove water and then breaking the dried mix into irregular shaped pieces.

In a method of making low density, porous articles for use in the production of silicon and ferrosilicon wherein a finely-divided silica-containing material is blended together with a finely-divided carbonaceous reducing agent, a binder and water to form a wet mix and wherein the wet mix is formed to the desired size and shape of said article;

• the improvement which comprises employing silica fume having a particle size of less than about 0.5 microns as a finely-divided silica-containing material and then forming said low density, porous articles by depositing the wet mix evenly in a relatively thin layer over a flat surface, drying the mix at elevated temperatures in order to remove water and then breaking the dried mix into irregular shape pieces.