Abrasion resistant silicone coated polycarbonate article

#This invention relates to non-opaque abrasion and chemical solvent resistant thermoset organopolysiloxane coated shaped polycarbonate articles wherein the organopolysiloxane top coat is uniformly and tenaciously adhered to the polycarbonate substrate. More particularly, the present invention relates to an organopolysiloxane coated polycarbonate article having a thermoset acrylic primer layer of controlled thickness disposed between the polycarbonate substrate and the organopolysiloxane top coat.

#The use of transparent glazing materials utilizing polycarbonate resin as a structural component for windows, windshields and the like are well known. While these polycarbonate resins are easily fabricated into the desired shape and have excellent physical and chemical properties, such as being less dense than glass and having more breakage resistance than glass, their abrasion and chemical solvent resistance is relatively low.

#In order to overcome this relatively low abrasion resistance and to otherwise improve the surface characteristics of the polycarbonate, various coatings have been applied onto the polycarbonate substrates. U.S. Pat. No. 3,582,398 describes a fabricated polycarbonate part having improved optical properties consisting of a polycarbonate substrate having a transparent coating thereon consisting of a thermoplastic polymethylmethacrylate. U.S. Pat. No. 4,061,652 describes a coating for polycarbonate resins comprised of (i) an acrylic resin which is a mixture of olefinically unsaturated organic monomers in combination with an acrylic polymer, and (ii) certain urethanes of hydroxygenzotriazoles and hydroxybenzophenones in combination with certain catalysts. U.S. Pat. Nos. 3,451,838, 3,986,997 and 4,027,073 disclose organopolysiloxane coating compositions and techniques for the application of these organopolysiloxane coatings onto polycarbonate surfaces. While these coatings have many desirable properties, e.g., they are hard, abrasion resistant, and chemical solvent resistant, these organopolysiloxane coatings do not in all instances possess the requisite degree of uniform adherence to and durability on these polycarbonate surfaces. U.S. Pat. No. 3,707,397 describes a process for providing a hard coating on, inter alia, polycarbonate articles, said process including priming the polycarbonate surface with an adhesion promoting thermosettable acrylic and applying an organopolysiloxane onto the primed surface. This reference further teaches that the thickness of the thermosettable acrylic polymer primer layer varies between 0.01 mil up to as much as 0.5 mil or even more.

#In order that those skilled in the art may better understand how the present invention may be practiced, the following examples are given by way of illustration and not by way of limitation.

#An aromatic polycarbonate is prepared by reacting 2,2-bis(4-hydroxyphenyl)propane and phosgene in the presence of an acid acceptor and a molecular weight regulator and having an intrinsic viscosity of 0.57. The product is then fed to an extruder, which extruder is operated at about 265.degree. C. and the extrudate is comminuted into pellets.

#The pellets are then injection molded at about 315.degree. C. into test panels of about 4 in. by 4 in. by about 1/8 in. thick. The test panels are subjected to an abrasion test. The abrasion test is one wherein test panels having a 1/4-inch diameter hole cut in the center are subjected to a Taber Abraser. The Taber Abraser is equipped with CS-10F wheels which are resurfaced every 200 cycles by abrading for 25 cycles on an S-11 refacing disc. The weights used in combination with the CS-10F wheels are 500 gm. weights. Initial measurements of % Haze are made at four places around the future wear track of the sample using a Gardner Hazemeter. The sample is abraded for 300 cycles, cleaned with isopropanol, and the % Haze is remeasured at the same four places. The four differences in % Haze are calculated and averaged to give the .DELTA.% Haze. The results of this abrasion test are set forth in Table I.