Lightweight porous aggregate comprising alkali metal borosilicoaluminate and process for the preparation thereof
OwnerJose Walls-Muyceloinventor
Life of this patent
Estimating the term…
Abstract
A lightweight aggregate comprising an alkali metal borosilicoaluminate, is in the form of discrete, porous and expanded particles of approximately spherical shape, has a specific weight between about 60 and about 600 kg/m.sup.3 and a compression strength of from about 140 kg/cm.sup.2 up to about 250 kg/cm.sup.2, is highly insoluble in water, steam, acids or bases, has a melting temperature above 1500.degree. C. and a low alkalinity, and chemically comprises a homogeneous admixture of acid, basic and amphoteric oxides. A highly preferred embodiment of the aggregate has an M.sub.2 O/B.sub.2 O.sub.3 ratio between about 3:1 to about 6:1, where M is an alkali metal.
Claims16
A lightweight aggregate comprising discrete, porous and expanded alkali metal borosilicoaluminate particles having an approximately spherical shape, said aggregate having a specific weight of between about 60 and 100 kilograms per cubic meter, and a melting temperature higher than about 1500.degree. C., said particles consisting essentially of a homogeneous admixture of acid, basic and amphoteric oxides, containing from about 20%-92% by weight of SiO.sub.2, from about 1% to about 18% by weight of B.sub.2 O.sub.3, from about 5% to about 60% by weight of M.sub.2 O, wherein M is an alkali metal, from about 1% to about 45% by weight of Al.sub.2 O.sub.3, and from about 1% to about 20% by weight of an additive, wherein the ratio of M.sub.2 O/B.sub.2 O.sub.3 is between 3:1 and about 6:1, and
- said aggregate having a compression strength of from about 140 to about 175 kilograms per square centimeter, being substantially insoluble in water, steam, acids and alkalies, and having an alkalinity equivalent to between about pH 8 and pH 9.
A process for making particulate lightweight porous aggregates which comprises:
- preparing an aqueous paste of an alkali metal hydroxide in admixture with a mineral containing aluminum oxide, silicon dioxide in mineral form, boric oxide, a volatile material and an aggregate modifier,
- stirring the aqueous paste and allowing the temperature to be autogenously increased to a temperature between about 70.degree. C. to 80.degree. C.,
- discontinuing the stirring action when said temperature remains unaltered for a short period of time and said paste forms a reaction mass,
- drying the reaction mass at a temperature of about 300.degree. C.,
- crushing the dried mass to form particles of the desired size,
- firing the particles up to a temperature of from about 650.degree. C. to 850.degree. C. to form expanded porous particles, and
- cooling the fired expanded porous particles to room temperature to form an aggregate having a specific weight of from about 140 to 250 kg/cm.sup.2 said aggregate being substantially insoluble in water, steam, acids or bases and having an alkalinity equivalent to a pH of about 8 to 9.
A process for making particulate lightweight porous aggregate which comprises:
- p1 preparing an aqueous paste of an alkali metal hydroxide or carbonate in admixture with suitable amounts of aluminum oxide in mineral form, boric oxide, a volatile material or a solvent, and a heavy metal oxide selected from the group consisting of iron, zinc, lead and titanium oxide in any of their mineral forms;
- stirring the aqueous paste and allowing the temperature to be autogenously increased to between about 70.degree. C. and 80.degree. C.;
- discontinuing the stirring action when said temperature remains unaltered for a short period of time to form a reaction mass;
- drying the reaction mass at a temperature of about 300.degree. C.;
- crushing the dried reaction mass to form particles;
- firing said particles at a temperature of from about 600.degree. to about 1,000.degree. C. to form expanded porous particles, and
- cooling the fired and expanded porous particles to room temperature to form an aggregate haing a specific weight of from about 60 to 600 kilograms per cubic meter, a compression strength of from about 140 to 250 kilograms per square caentimeter, said aggregate being substantially insoluble in water, steam, acids or bases, having a pH of between about 8 and 9, and containing from about 20 to about 92% by weight SiO.sub.2, 1 to 60% by weight of B.sub.2 O.sub.3, 5 to 60% by weight M.sub.2 O wherein M is an alkali metal, 1 to 45% by weight Al.sub.2 O.sub.3 and 1 to 20% by weight of at least one of said volatile material or said heavy metal oxide.
Dependencies are inferred from the claim text.