Process for the production of elemental silver from silver chloride or silver sulphate

#This invention relates to the production of elemental silver from silver chloride or silver sulphate.

#In the hydrometallurgical treatment of silver-containing materials, silver chloride or silver sulphate are frequently produced. Known methods for the production of elemental silver from these salts have various disadvantages. One known method is to heat silver chloride with metallic zinc powder, but metallic zinc powder is expensive and the silver product is unduly contaminated with zinc. Further, a temperature of about 1100.degree. C. is required for this reaction, and at this temperature the reduced metallic silver tends to react with a ceramic or metallic reaction vessel, thereby further contaminating the silver.

#It has also been proposed to reduce an aqueous suspension of silver chloride in the presence of metallic zinc powder or silver ammine sulphate solution with hydrogen gas. However, the hydrogen reagent is also relatively expensive and the reaction has to be carried out under pressure in an autoclave.

#It is therefore an object of the invention to provide an improved process for the recovery of elemental silver from silver chloride or silver sulphate.

#The present invention is based on the discovery that elemental silver in the form of fine powder can be produced by mixing silver chloride or silver sulphate with sodium carbonate, and heating the mixture at a temperature in the range of from about 500.degree. C. to about 650.degree. C. to effect a solid state reaction. The reaction is usually complete relatively quickly, for example in about one hour, and the silver powder produced does not significantly react with a ceramic or suitable metallic reaction vessel. Sodium chloride or sodium sulphate is also produced in the reaction and, together with any unreacted sodium carbonate, may readily be removed by washing with water. The other reaction products are carbon dioxide and oxygen which are of course harmless gases. The silver product is usually directly obtained as a fine powder. Some slight sintering may occur at a temperature above about 625.degree. C., but this can readily be broken up.

#In the case of silver chloride, the mixture is preferably heated at a temperature over about 570.degree. C. to ensure completeness of the reaction and below about 625.degree. C. to lessen the likelihood of sintering. In the case of silver sulphate, the reaction does take place substantially at a lower temperature than in the case of silver chloride, and thus the temperature range of from about 500.degree. C. to about 550.degree. C. is preferred in the case of silver sulphate.