Insulating coating for transformer wires
AssigneeGeneral Electric Company
InventorRalph G. Flowers
Life of this patent
Estimating the term…
Abstract
Improved three component insulating coatings for both wet solvent and dry electrostatic application to transformer wires contain an increased eopoxy resin concentration and a decreased amount of polyvinyl acetal and phenol aldehyde resins. The increased epoxy content gives substantially improved coatings with no adverse dissipation and hydrolytic effects. The epoxy constituent can range from 30-60 per cent by weight providing the ratio of the polyvinyl acetal to phenol aldehyde is kept within the range from 1 to 1 to 2 to 1.
Claims2
An improved transformer insulating wire coating composition of the type containing phenol aldehyde resin, polyvinyl acetal resin, and epoxy resin, the improvement which comprises the composition defined within the accompanying triaxial diagram of FIG. 5 and and including 1 to 10 percent by weight of said epoxy resin of an epoxy curing agent.
An improved transformer insulating coating composition of the type containing phenol aldehyde resin, polyvinyl acetal resin, and epoxy resin the improvement which comprises:
- 30 to 60 weight percent of the epoxy resin and a ratio of the polyvinyl acetal to the phenol aldehyde within a range of 1.10 to 1.90, and 1 to 10 percent by weight of said epoxy resin of an epoxy curing agent.
Dependencies are inferred from the claim text.