Two component aqueous based coating composition

AssigneeCelanese Corporation

InventorsDavid A. Shimp, Darrell D. Hicks, Richard B. Graver

Life of this patent

Estimating the term…

Loading patent…

Abstract

The present invention provides a two component resin coating system which when mixed forms a curable coating composition. The first component comprises a polyamine terminated polyepoxide adduct which has been salted with a controlled amount of acid. The salted product is dissolved in a co-solvent having a specifically defined solubility parameter polar component and water. The second component comprises a low molecular weight water insoluble polyepoxide crosslinker which is optionally dissolved in the selected co-solvent. When the two-components are blended together, the polyepoxide resin crosslinker is dispersed in the microemulsified state throughout the salted adduct solution and the resulting composition exhibits improved pot life, freeze thaw stability, and film forming properties.

Claims13

Dependent claims

A two component resin coating system which when the components are mixed forms a thermosetting curable coating composition having the resin of the second component present in said mixture in the microemulsified state which comprises:

(A) as a first component, the solution of:
(1) an acid salt of a polyamine terminated polyepoxide adduct which is the reaction product of
(a) a polyepoxide resin represented by the structural formula:
##STR5## wherein R is a divalent hydrocarbon radical of a dihydric phenol and the average value of n is from 8 to 20 and
(b) a polyamine having at least two amine nitrogen atoms per molecule, at least three reactive amine hydrogen atoms per molecule and no other groups reactive with epoxide groups,
wherein about 1 mol of (b) is reacted with each epoxide equivalent of (a), said adduct having an active amine hydrogen equivalent weight of about 290 to about 1000 and an amine nitrogen equivalent weight of about 360 to about 1500;
(2) at least one organic aliphatic hydroxyl containing co-solvent having a solubility parameter polar component between about 2.6 and about 3.9 (cal/cm.sup.3).sup.1/2 present in an amount of from about 5 to about 45% by weight based on the weight of the polyepoxide-amine adduct and co-solvent;
and
(3) water in an amount sufficient to bring the solids content of the mixture to below 40% by weight, based on the weight of adduct, co-solvent and water and wherein said solution has a pH of about 4 to about 5;
(B) as a second component a polyepoxide cross-linker which is a glycidyl polyether of a polyhydric phenol having an epoxide equivalent weight of about 150 to about 500, said first component (A) and said second component (B) being present in the amounts to achieve an epoxide group to active hydrogen ratio of from about 0.25:1 to about 1.5:1 and wherein A and B are present in the weight ratio of about 3.5:1 to about 1:1.

7 more elements

A process for preparing a curable thermosetting coating composition which comprises:

(A) intimately admixing;
(1) an acid salt of a polyamine terminated polyepoxide adduct which is the reaction product of
(a) a polyepoxide resin represented by the structural formula:
##STR7## wherein R is a divalent hydrocarbon radical of a dihydric phenol and the advangtage value of n is 8 to 20;
and
(b) a polyamine having at least 2 amine nitrogen atoms per molecule at least three reactive amine hydrogen atoms per molecule and no other groups reactive with epoxide groups,
wherein about 1 mol of (b) is reacted with each epoxide equivalent of (a), said adduct having an active amine hydrogen equivalent weight of about 290 to about 1000 and an amine nitrogen equivalent weight of about 360 to about 1500;
(2) at least one organic aliphatic hydroxyl containing co-solvent having a solubility parameter polar component of from about 2.6 to about 3.9 (cal/cm.sup.3).sup.1/2 ;
and
(3) water;
to form a first component wherein the co-solvent is present therein in an amount of from about 5 to about 45% by weight, based on the weight of adduct and co-solvent, the water is present therein in an amount sufficient to achieve a solids content below 40% by weight, based on the weight of adduct co-solvent and water;
and the pH of the mixture is about 4 to about 5;
and
(B) admixing with said first component a polyepoxide resin crosslinker which is a glycidyl polyether of a polyhydric phenol having an epoxide equivalent weight of about 150 to about 500, the amount of said cross-linker in the second component being sufficient to achieve an epoxy to adduct amine hydrogen ratio of from amount 0.25:1 to about 1.5:1, and wherein A and B are present in the weight ratio of about 3.5:1 to about 1:1, to form a final composition wherein the epoxy resin crosslinker is present therein in the microemulsified state.
(C) controlling the amount of water in the final composition in a manner sufficient to achieve a solids content in the final composition of from about 5 to about 40%, by weight, based on the weight of adduct, crosslinker, co-solvent and water.