Intumescent flame-resistant coating
AssigneeRockwell International Corporation
InventorsCharles L. Hamermesh, Chiang-Ying M. Tung, Peter A. Hogenson
Life of this patent
Estimating the term…
Abstract
A plastic coating is provided which protects coated structures from flame. The coating is a product resulting from mixing an aromatic polyisocyanate, an aromatic polycarboxylic compound, and furfuryl alcohol at a temperature less than 80.degree. C. The structure to be protected from flame is coated with the product and the product is then dried. If the coated structure is exposed to flame, the coating intumesces to form a flame-resistant foam which protects the structure.
Claims8
A method of improving the flame resistance of a structure comprising the steps of:
- providing an aromatic polyisocyanate;
- providing an aromatic polycarboxylic compound;
- providing furfuryl alcohol;
- mixing said aromatic polyisocyanate, said aromatic polycarboxylic compound, and said furfuryl alcohol in the range of:
- 20 to 60% aromatic polyisocyanate, 10 to 40% aromatic polycarboxylic compound and 25 to 60% furfuryl alcohol;
- coating a surface of the structure with the product of said mixing step;
- and
- drying said product, said steps of mixing, coating and drying being accomplished at less than 80.degree. C., whereby said product forms a coating which intumesces when heated to form a polyimide foam.
A method of improving the flame resistance of a structure, comprising the steps of:
- providing polymethylene polyphenylisocyanate;
- providing pyromellitic deanhydride;
- providing furfuryl alcohol;
- providing a surfactant;
- mixing said polymethylene polyphenylisocyanate, said pyromellitic dianhydride, and said furfuryl alcohol in the range of:
- 20 to 60% polymethylene polyphenylisocyanate, 10 to 40% pyromellitic dianhydride, and 25 to 60% furfuryl alcohol, and 2 to 5% surfacant;
- coating a surface of the structure with the product of said mixing step;
- and
- drying said product, said steps of mixing, coating, and drying being accomplished at less than 80.degree. C., whereby said product forms a coating which intumesces when heated to form a polyimide foam.
A structure having a coating which intumesces when heated to form a polyimide foam, comprising:
- a substrate;
- a coating on said substrate, said coating comprising a product resulting from mixing 20 to 60% of an aromatic polyisocyanate with 10 to 40% of an aromatic polycarboxylic compound with 25 to 60% furfuryl alcohol, said product being maintained at a temperature less than approximately 80.degree. C.
A structure having a coating which intumesces when heated to form a polyimide foam, comprising:
- a substrate;
- a coating on said substrate, said coating comprising a product resulting from mixing 20 to 60% polymethylene polyphenylisocyanate with 10 to 40% pyromellitic dianhydride, 25 to 60% furfuryl alcohol, and 2 to 5% surfactant, said product being maintained at a temperature less than approximately 80.degree. C.
A structure having a coating which intumesces when heated to form a polyimide foam, comprising:
- a substrate;
- a coating on said substrate, said coating comprising a product resulting from mixing 20 to 60% polymethylene polyphenylisocyanate with 10 to 40% benzophenone-3,3'4,4'-tetracarboxylic acid dianhydride (BTDA), 25 to 60% furfuryl alcohol, and 2 to 5% surfactant, said product being maintained at a temperature less than approximately 80.degree. C.
A method of improving the flame resistance of a structure, comprising the steps of:
- providing polymethylene polyphenylisocyanate;
- providing benzophenone-3,3'4,4-tetracarboxylic acid dianhydride (BTDA);
- providing furfuryl alcohol;
- providing a surfactant;
- mixing said polymethylene polyphenylisocyanate, said BTDA, and said furfuryl alcohol in the range of:
- 20 to 60% polymethylene polyphenylisocyanate, 10 to 40% BTDA, and 25 to 60% furfuryl alcohol, and 2 to 5% surfactant;
- coating a surface of the structure with the product of said mixing step;
- and
- drying said product, said steps of mixing, coating, and drying being accomplished at less than 80.degree. C., whereby said product forms a coating which intumesces when heated to form a polyimide foam.
Dependencies are inferred from the claim text.