Continuous casting mold flux powders
AssigneeThe Clay Harden Company
InventorGeorge F. Carini
Life of this patent
Estimating the term…
Abstract
This invention relates to mold flux powders for the continuous casting of steel. The mold flux powders comprise a plurality of sequential melting systems forming successive melts each of which assimilates the ingredients of the next system into the melt. In this way, the desired fludity is achieved in the mold flux at a rate required by the particular continuous casting process in which the flux is being used without resorting to an excessively low melting flux. At least one of the systems comprises a finely-divided glass.
Claims7
In the continuous casting of steel wherein the steel is teemed from a tundish to a continuous casting mold, the improvement comprising introducing to said mold during teeming, a mold flux powder, consisting essentially of, in weight percent, at least three sequentially melting systems,
- the first system comprising 10 to 30 percent of one or more glasses having softening point temperature between 1200.degree. and 2000.degree. F.,
- the second system comprising 10 to 30 percent cryolite, fluorspar, sodium fluoride and mixtures thereof,
- the third system comprising 40 to 80 percent of a mixture of Portland Cement and whiting, the weight ratio of whiting to Portland Cement in the mold flux powder being up to about 0.5,
- whereby the fusion point, rate of fusion and fluidity can be tailored to a particular continuous casting process involved.
In the continuous casting of steel wherein the steel is teemed from a tundish to a continuous casting mold, the improvement comprising introducing to said mold during teeming, a mold flux powder, consisting essentially of, in weight percent, at least three sequentially melting systems,
- the first system comprising 10 to 30 percent of one or more glasses having softening point temperatures between 1200.degree. and 2000.degree. F.,
- the second system comprising 10 to 30 percent fluorspar, and
- the third system comprising 40 to 80 percent of a mixture of Portland Cement and whiting, the weight ratio of whiting to Portland Cement in the mold flux powder being up to about 0.5,
- whereby the fusion point, rate of fusion and fluidity can be tailored to the particular continuous casting process involved.
A composition of matter useful as a flux consisting essentially of, by weight
- 40 to 80 percent of a mixture of whiting and Portland Cement in a weight ratio up to about 0.5,
- 10 to 30 percent of fluorspar, cryolite and sodium fluoride and mixtures thereof,
- 10 to 30 percent by weight of one or more glasses,
- said glasses analyzing, by weight percent
- Na.sub.2 O-- 8 to 25;
- K.sub.2 O-- up to 8;
- B.sub.2 O.sub.3 -- 0 to 25;
- SiO.sub.2 -- 20 to 75;
- F.sub.2 -- 0 to 8;
- CaO-- 10 to 30;
- BaO-- 0 to 15;
- and Al.sub.2 O.sub.3 -- 0 to 3.
Dependencies are inferred from the claim text.