Beam lead Schottky barrier diode for operation at millimeter and submillimeter wave frequencies
AssigneeEaton Corporation
InventorJoseph A. Calviello
Life of this patent
Estimating the term…
Abstract
A beam lead gallium arsenide diode having a rectangular junction perimeter conforming to that the beam lead, recovers ninety-five percent of the junction current and provides an almost perfect ideality factor of 1.07. This device is formed on a semi-insulating substrate to provide for isolation from adjacent devices on the same substrate and for confining the current to a direct path from the junction to an immediately adjacent ohmic contact. An extremely small junction area necessary for operation at millimeter wave frequencies is formed by special processing which includes the use of dry etching and the fabrication of the junction prior to passivation.
Claims3
A process for producing a Schottky barrier junction device comprising the following steps:
- (a) supplying a substrate with an N+layer covered with an N layer,
- (b) depositing a first layer of tantalum on the N layer to form a Schottky barrier junction,
- (c) depositing a first layer of gold over the tantalum layer,
- (d) depositing a layer of molybdenum over the first gold layer,
- (e) depositing a second layer of gold over the molybdenum,
- (f) depositing a layer of photoresist over the second layer of gold,
- (g) exposing and developing the photoresist to define the junction area by exposing the second layer of gold in the junction area,
- (h) depositing a layer of chromium over the photoresist and the exposed junction area of the second gold layer,
- (i) removing the photoresist to provide a chromium mask over the junction area,
- (j) etching the second gold layer away except where it is protected by the chromium mask in the junction area,
- (k) etching the molybdenum layer away except in the junction area,
- (l) etching through a portion of the first gold layer away from the junction area,
- (m) etching the molybdenum layer to produce an undercut about its periphery within the junction area,
- (n) etching through the remainder of the first gold layer in the area away from the junction area,
- (o) etching away the first tantalum layer except in the junction area,
- (p) etching into the N layer except in the junction area to produce a mesa in the N layer in the junction area,
- (q) depositing a layer of passivation over the device except on the under-cut molybdenum layer which is shielded from this deposition by the gold and chromium layers above the molybdenum layers,
- (r) etching through the molybdenum layer left unprotected by the absence of the passivation layer, and
- (s) removing the second layer of gold and the chromium layers after etching through the molybdenum layer.
Dependencies are inferred from the claim text.