OwnerTeruhisa Kondo, Jiro Ishiguro +1inventors
InventorsTeruhisa Kondo, Jiro Ishiguro, Nobuatsu Watanabe
Life of this patent
Estimating the term…
Abstract
Novel metal salts of boric acid esters of saccharides have been found to be extremely useful for imparting a high oxidation-resistance to carbonaceous materials. The metal salts of the boric acid esters according to the present invention are water-soluble and can be easily formulated into aqueous solutions thereof. Therefore, the treatment of carbonaceous materials can be easily, simply done using an aqueous solution of the present metal salt of the boric acid ester.
Claims5
An antioxidant for a carbonaceous material such as graphite or carbon which comprises at least one metal salt of a boric acid ester of a member selected from the group consisting of sorbitol, mannitol, sucrose, maltose, lactose and combinations thereof, said boric acid ester containing boric acid values in an amount of about 0.5 to 2.0 moles per mole of said member selected from the group consisting of sorbitol, mannitol, sucrose, maltose, lactose and combinations thereof, said metal being a member selected from the group consisting of magnesium, calcium, zinc and barium and being contained in an amount of about 1 to 3 atomic moles per mole of said boric acid ester.
A process for the preparation of an antioxidant for a carbonaceous material such as graphite or carbon which comprises the steps of (1) reacting a member selected from the group consisting of sorbitol, mannitol, sucrose, maltose, lactose and mixtures thereof with boric acid at about 105.degree. to 130.degree. C. for 2 to 5 hours, said boric acid being employed in an amount of about 0.5 to 2.0 moles per mole of said member selected from the group consisting of sorbitol, mannitol, sucrose, maltose, lactose and mixtures thereof, and (2) subsequently reacting the resulting boric acid ester with at least one compound of a metal selected from the group consisting of magnesium, calcium, zinc and barium at a temperature of about room temperature to about 100.degree. C. for a sufficient time to complete the reaction, said compound of a metal being employed in an amount of about 1 to 3 moles in terms of amount of metal oxide per mole, in terms of amount of boric acid anhydride, of the boric acid ester.
A method of rendering graphite or carbon resistant to oxidation which comprises contacting graphite or carbon with an antioxidant comprising at least one metal salt of a boric acid ester of a member selected from the group consisting of sorbitol, mannitol, sucrose, maltose, lactose and combinations thereof for a sufficient time for said antioxidant to permeate the carbonaceous material, said boric acid ester containing boric acid values in an amount of about 0.5 to 2.0 moles per mole of said member selected from the group consisting of sorbitol, mannitol, sucrose, maltose, lactose and combinations thereof, said metal being a member selected from the group consisting of magnesium, calcium, zinc and barium and being contained in an amount of about 1 to 3 atomic moles per mole of said boric acid ester, ester, and subsequently subjecting said graphite or carbon to heat treatment at about 400.degree. to about 1,300.degree. C. for a sufficient time for said at least one metal salt to form a glassy compound.