Adhesion of polyamide or polyester cords to rubber
AssigneeThe General Tire & Rubber Company
InventorTerry C. Neubert
Life of this patent
Estimating the term…
Abstract
An aqueous alkaline dispersion of a rubbery graft low gel vinyl pyridine copolymer and a water soluble, heat reactive phenolic resin is useful in forming an adhesive for bonding polyamide or polyester reinforcing elements or cords to rubber compounds or stocks. After dipping the polyamide or polyester cord in the one-step adhesive dip, the coated cord is heated to dry it and heat cure or heat set the adhesive on the cord. Thereafter, the adhesive containing polyamide or polyester cord is combined with, or laminated to (calendered), a curable rubber compound and the resulting assembly is cured to form a composite in which the polyamide or polyester cord is bonded to the rubber by means of said adhesive.
Claims8
A method for adhering a polyamide or polyester reinforcing element to a rubber compound which comprises treating said element with an aqueous alkaline dispersion of about 10 to 30% by weight of solids comprising on a dry weight basis 100 parts by weight of a rubbery graft low gel vinyl pyridine copolymer consisting essentially of
- (a) a core of a copolymer of butadiene-1,3 and styrene in the parts by weight of ratio of butadiene-1,3 to styrene of about 40:60 to 60:40 and having a gel content of from about 0 to below 40% and
- (b) a shell of a copolymer of butadiene-1,3 and a vinyl pyridine and having a gel content of from about 0 to below 70% and
- (c) where in said graft copolymer the total amount of said monomers is from about 47 to 69% by weight of butadiene-1,3, from 23 to 52% by weight of styrene and from 1 to 8% by weight of the vinyl pyridine, and a water-soluble thermosetting phenolic-aldehyde resin in an amount of from about 10 to 40 parts by weight, heating said treated element at a temperature of from about 300.degree. to 500.degree. F. for from about 150 to 30 seconds to remove essentially all of the water from said dispersion and to provide said element with a heat set adhesive in an amount of from about 3 to 15% by weight (dry) based on the weight of said reinforcing element, combining said dried and heat set adhesive containing reinforcing element with an unvulcanized vulcanizable rubber compound and vulcanizing the same.
A bonded composite material comprising a polyamide or polyester reinforcing element embedded in a vulcanized rubber, said element containing from about 3 to 15% by weight dry based on the weight of said element of a heat cured adhesive composition useful for adhering said element to a rubber compound comprising on a dry weight basis 100 parts by weight of a rubbery graft low gel vinyl pyridine copolymer consisting essentially of
- (a) a core of a copolymer of butadiene-1,3 and styrene in the parts by weight ratio of butadiene-1,3 to styrene of about 40:60 to 60:40 and having a gel content of from about 0 to below 40% and
- (b) a shell of a copolymer of butadiene-1,3 and a vinyl pyridine and having a gel content of from about 0 to below 70% and
- (c) where in said graft copolymer the total amount of said monomers is from about 47 to 69% by weight of butadiene-1,3, from 23 to 52% by weight of styrene and from 1 to 8% by weight of the vinyl pyridine, and a water-soluble thermosetting phenolic-aldehyde resin in an amount of from about 10 to 40 parts by weight.
Dependencies are inferred from the claim text.