Method of manufacturing a grate
OwnerVernon F. Plassinventor
Life of this patent
Estimating the term…
Abstract
A method of manufacturing a grate for support of combustible solids comprises mixing a kaolin-type clay with water and a small percentage of stainless steel needles, pouring the mixture into a prepared mold, allowing the mixture to harden, drilling holes through the hardened mixture for the purpose of allowing air to pass therethrough, and curing the hardened mixture at an elevated temperature. The curing of the hardened mixture is preferably accomplished by increasing the temperature gradually to a maximum of 2,000.degree. F. and slowly decreasing the temperature to an ambient temperature.
Claims7
A method of manufacturing a grate for support of a combustible solid comprising the following steps:
- (a) mixing a kaolin-type clay with about 10.4 percent of its weight of water;
- (b) adding gradually stainless steel needles having the dimension of about 0.010 inches by 0.022 inches by 1 inch in the amount of 11/2 percent of the weight of kaolin-type clay;
- (c) mixing the resulting material thoroughly for about 5 minutes;
- (d) pouring the mixture into prepared molds while vibrating for proper consistency;
- (e) allowing the molds to stand at ambient temperature for about 15 hours to harden;
- (f) drilling alternate rows of perpendicular and non-perpendicular through holes having a diameter of 1/4 inch on 2 inch centers, the non-perpendicular through holes forming an angle of 15 degrees in the longitudinal direction with respect to a perpendicular;
- (g) placing the drilled product in a curing oven at 100 degrees F.;
- (h) increasing the oven temperature at a rate of 50 degrees per hour until the oven temperature reaches 1000 degrees F.;
- (i) maintaining the oven temperature at 1000 degrees F. for about 8 hours;
- (j) increasing the oven temperature 100 degrees per hour until the oven temperature reaches 2000 degrees F.;
- and
- (k) decreasing the oven temperature gradually to an ambient temperature.
A method of manufacturing a grate for support of combustible solids comprising the following steps:
- (a) mixing a kaolin-based clay with water;
- (b) adding to the mixture metallic needles approximately one inch in length;
- (c) pouring the clay and metallic needle mixture into a prepared mold;
- (d) allowing the mold to harden;
- (e) drilling holes through the hardened molded mixture;
- and
- (f) curing the drilled product at elevated temperatures.
Dependencies are inferred from the claim text.