Production of .beta.-alumina ceramic tubes
AssigneeGeneral Electric Company
InventorsVincent J. DeCarlo, Robert W. Powers, Stephan P. Mitoff
Life of this patent
Estimating the term…
Abstract
A sintered .beta.-alumina cylindrical tube of uniform shape is produced by placing the unsintered tube within a sagger, passing the sagger on friction-reducing balls through a horizontal firing tube and continuously alternately rotating the tube-containing sagger through the firing tube so that all portions of the tube therewithin experience on the average the same gravitational effect.
Claims20
A method for producing a sintered polycrystalline ceramic hollow cylindrical tube open at least on one end without significant out-of-roundness which comprises shaping ceramic powder into a hollow green cylindrical tube, providing a cylindrical sagger open at least on one end and having an inner volume at least sufficient to accommodate said green tube substantially horizontally and allow said tube to rotate therein, disposing said green tube substantially horizontally within said sagger, providing a substantially horizontally disposed open-ended firing tube containing a sintering zone, positioning a layer of friction-reducing spheres on the surface of the lower portion of said horizontally-disposed firing tube along the length thereof, providing said firing tube with an atmosphere which has no significant deleterious effect on said tube being sintered, heating said sintering zone to sintering temperature, passing said tube-containing sagger through said firing tube on said spheres, continuously and simultaneously advancing and alternately rotating said tube-containing sagger through said firing tube so that all portions of said tube therewithin are subjected to at least substantially the same gravitational effect, said advancement and alternate rotation having no significant deleterious effect on said tube therewithin, one completed alternate rotation being comprised of a rotation and a counter-rotation in predetermined amounts, the angles of all said rotations being substantially equal, the angles of all said counter-rotations being substantially equal, the rate of said alternate rotation being at least sufficient to make at least one completed alternate rotation of said tube within said sagger in an advancing distance equivalent to the outer circumference of said tube within said sagger, said tube-containing sagger being advanced through said sintering zone at a rate at least sufficient to sinter said tube therewithin.
A method for producing a sintered polycrystalline cylindrical hollow tube open at least on one end of .beta.-alumina, .beta."-alumina and mixtures thereof without significant out-of-roundness which comprises shaping a green hollow cylindrical tube from .beta.-alumina powder or a mixture of reactant powders which react to produce .beta.- and/or .beta."-alumina at an elevated temperature below or at sintering temperature, said green tube being open at least on one end, providing a cylindrical sagger open at least on one end and having an inner volume at least sufficient to accommodate said green tube substantially horizontally and allow said tube to rotate therein, disposing said green tube substantially horizontally within said sagger, providing a substantially horizontally-disposed open-ended firing tube containing a sintering zone, positioning a layer of friction-reducing spheres on the surface of the lower portion of said horizontally-disposed firing tube along the length thereof, providing said sintering zone with a non-reducing dry atmosphere which has no significant deleterious effect on said tube being sintered, heating said sintering zone to a sintering temperature ranging from about 1525.degree. C. to about 1825.degree. C., passing said tube-containing sagger through said firing tube on said spheres, continuously and simultaneously advancing and alternately rotating said tube-containing sagger through the firing tube so that all portions of said tube therewithin are subjected to at least substantially the same gravitational effect, said advancement and alternate rotation having no significant deleterious effect on said tube therewithin, one completed alternate rotation being comprised of a rotation and a counter-rotation in predetermined amounts, the angles of all said rotations being substantially equal, the angles of all said counter-rotations being substantially equal, the rate of said alternate rotation being at least sufficient to make at least one completed alternate rotation of said tube within said sagger in an advancing distance equivalent to the outer circumference of said tube within said sagger, said tube-containing sagger being advanced through said sintering zone at a rate appropriate to sinter said tube therewithin to a density of at least 95% of the theoretical density of .beta.-alumina.
Dependencies are inferred from the claim text.