Method of producing silicate binders and coatings
AssigneeRust-Oleum Corporation
InventorsKenneth H. Brown, Kenneth M. Wolma
Life of this patent
Estimating the term…
Abstract
An improved method of preparing hydrolyzed alkyl silicate binders useful in manufacturing protective coatings, i.e., zinc-rich coatings, is described wherein the hydrolysis is catalyzed in the presence of a strong acid form ion exchange resin instead of a conventional acid catalyst.
Claims7
A method of making a hydrolyzed alkyl silicate binder which comprises:
- a. dissolving an alkyl silicate, wherein the alkyl groups range from 1 to 4 carbon atoms, in an organic solvent containing sufficient anhydrous strong acid form ion exchange resin to effectively catalyze the hydrolysis reaction;
- and
- b. adding a quantity of water of an amount sufficient to provide 0.125 to 0.475 moles of water for each alkoxy group carried by the alkyl silicate,
- and c. removing the ion exchange resin after the reaction is completed.
A method of making a zinc-rich coating which comprises:
- a. dissolving an alkyl silicate, wherein the alkyl groups range from 1 to 4 carbon atoms, in an organic solvent containing sufficient anhydrous strong acid form ion exchange resin to effectively catalyze the hydrolysis reaction of the alkyl silicate;
- b. adding a quantity of water of an amount sufficient to provide 0.125 to 0.475 moles of water for each alkoxy group carried by the alkyl silicate;
- c. removing the ion exchange resin after the reaction is completed;
- d. adding a quantity of pigments and rheological additives dispersed in anhydrous organic solvent;
- and
- e. adding a quantity of finely divided zinc dust.
In a method of making zinc-rich coatings which comprises dissolving tetraethyl orthosilicate in an organic solvent, adding a quantity of an acidic catalyst to the solution whereby to adjust the pH to the range of 1.5 to 4.0, adding a quantity of water to the solution, such quantity being in the range of 0.25 to 0.95 of an equivalent weight with respect to the quantity of tetraethyl orthosilicate to produce a liquid siloxane having an average chain length of 5 to 10 silicon atoms, agitating the mixture until an exothermic reaction is initiated, continuing agitation until the exothermic reaction is completed and the temperature of the solution begins to subside, and adding finely divided zinc dust to the resulting fluid;
- the improvement comprising as said catalyst, an anhydrous strong acid-form ion exchange resin capable of giving up its labile hydrogen ions, followed by the removal of the ion exchange resin after the exothermic reaction is complete and before the zinc dust is added.
Dependencies are inferred from the claim text.