Method of making crude boric acid from borate and sulfuric acid
AssigneeHJH Chemicals, Inc.
InventorJames R. Blasius
Life of this patent
Estimating the term…
Abstract
For the conversion of sodium tetraborate (e.g. "5 mole borax" or sodium tetraborate pentahydrate) to a solid, particulate mass of flame-retardant chemical, using little or no water, 0.95 to 0.98 mole of sulfuric acid is added to convert the tetraborate to a moist, particulate mixture of boric acid and sodium sulfate. The moist particulate mixture is suitable for imparting flame retardancy to cellulosic insulation; preferably, however, it is first dried to <20 wt.-% moisture.
Claims10
A method for making an essentially dry, free-flowing particulate mixture comprising boric acid and sodium sulfate, said method comprising the steps of:
- a. introducing sodium tetraborate into a mixing zone;
- b. introducing 0.95-0.98 mole of sulfuric acid and exothermically reacting said sulfuric acid with said sodium tetraborate to obtain a mixture of sodium sulfate and boric acid;
- c. maintaining the temperature of said mixing zone above 100.degree. C. but below about 150.degree. C. until a generally free-flowing, moist, particulate mixture is obtained.
A method for converting sodium tetraborate to a solid, particulate fire retardant mixture containing solid, particulate boric acid and sodium sulfate, said method comprising the steps of:
- (a) diluting about 0.95 to about 0.98 mole of sulfuric acid with a slurrying amount of water, and
- (b) blending, in a blending zone, the thus-diluted sulfuric acid with each mole of the sodium tetraborate, thereby forming a reaction medium in the blending zone,
- (c) maintaining the temperature of said reaction medium generally within the range of about 100.degree. to about 175.degree. C.,
- (d) recovering from the blending zone a solid, particulate fire retardant mixture which has been dried by the reaction exotherm of the reaction medium but retains a moisture content in excess of 20% by weight.
A method for converting sodium tetraborate to a solid, particulate fire retardant mixture containing solid, particulate boric acid and sodium sulfate, said method comprising the steps of:
- (a) blending, in a blending zone, sufficient concentrated sulfuric acid of at least 90% by weight H.sub.2 SO.sub.4 content with the sodium tetraborate to provide about 0.95 to about 0.98 mole of sulfuric acid for each mole sodium tetraborate, whereby the amount of water present in said blending zone is not sufficient to form a uniform slurry,
- (b) maintaining the temperature in said blending zone generally within the range of about 100.degree. to about 175.degree. C., and
- (c) recovering from the blending zone a generally dry, free-flowing particulate fire-retardant mass containing sodium sulfate and at least 30% by weight B.sub.2 O.sub.3, generally as boric acid.
Dependencies are inferred from the claim text.