Method of determining the deterioration of heat-resistant ferritic steel parts
AssigneeTokyo Shibaura Denki Kabushiki Kaisha
InventorsShuichi Komatsu, Shinichi Nakamura, Kazumi Shimotori, Yoshio Nakayama
Life of this patent
Estimating the term…
Abstract
A method of determining the degree of deterioration of a heat-resistant ferritic steel part, such as that of Cr-Mo-V steel practically applied in a region of high temperature from at least one of the crystallization factors such as the particle size, interparticle distance and crystallization density of a carbide, particularly V.sub.4 C.sub.3 crystallized out in said ferritic steel part.
Claims3
A method of determining the degree of deterioration of a Cr-Mo-V ferritic steel part applied in a region of high temperature which comprises the steps of:
- measuring the value of at least one of the crystallization factors of vanadium carbide, V.sub.4 C.sub.3, crystallized out in the Cr-Mo-V ferritic steel part applied in a region of high temperature, wherein said crystallization factors of vanadium carbide are particle size, interparticle distance, percentage volume or crystallization density, and wherein said crystallization density, and wherein said crystallization factors are measured from the structural image of said crystallized V.sub.4 C.sub.3 produced by the dark view field process of an electronic microscope;
- applying a previously obtained referential deterioration curve showing the relationship between the length of time for which the Cr-Mo-V steel is applied under test-accelerating conditions and said at elast one of the crystallization factors of vanadium carbide to determine the length of time under test-accelerating conditions necessary to produce the measured value of said at least one crystallization factor of vanadium carbide;
- and
- calculating the length of time for the steel part to be used under practical operating conditions from the length of time for which the steel is applied under test accelerating conditions to achieve the value shown by said at least one crystallization factor by applying the Larson-Miller parameter
- P=T (log t+20)
- wherein
- P=a constant,
- T=absolute temperature, and
- t=time.
A method of determining the degree of deterioration of a Cr-Mo-V ferritic steel part applied in a region of high temperature which comprises the steps of:
- measuring the value of at least one of the crystallization factors of vanadium carbide, V.sub.4 C.sub.3, crystallized out in the Cr-Mo-V ferritic steel part applied in a region of high temperature, wherein said crystallization factors of vanadium carbide are particle size, interparticle distance, percentage volume or crystallization density, and wherein said crystallization factors are measured from the structural image of said crystallized V.sub.4 C.sub.3 produced by the dark view field process of an electronic microscope;
- and
- applying a previously obtained referntial deterioriation curve showing the relationship between the Larson-Miller parameter
- P=T (log t+20)
- wherein
- P=a constant,
- T=absolute temperature, and
- t=time
- and said at least one of the crystallization factors of vandium carbide to determine the length of time newcessary to produce the measured value of said at least one crystallization factor of vanadium carbide.