Preparation of finely divided polyolefin molding materials containing conductive carbon black, and their use for the production of moldings

A process for the preparation of finely divided polyolefin molding materials which contain conductive carbon black and comprise

• (a) 100 parts by weight of a finely divided partially crystalline polyolefin which has a mean particle diameter of from 10 to 5,000 .mu.m and an intrinsic viscosity [.eta.], measured in decalin at 130.degree. C., of from 0.5 to 15, and
• (b) from 1 to 30 parts by weight of a conductive carbon black which has a mean particle diameter of from 10 to 50 nm,
• (c) with or without conventional amounts of other additives or auxiliaries,
• wherein components (a) and (b), with or without (c), are mixed, in a first stage (I), in a mixer, with or without supply or removal of heat, during which first stage (I), in a first sub-stage (I.1) the mixture is brought, at a mixing intensity of from 100 to 500 W/l of useful capacity, and within a period of from 2 to 50 minutes, from ambient temperature, which is below the crystallite melting point of the polyolefin (a) and is, in particular, room temperature, to the crystallite melting point of the polyolefin (a), and is immediately thereafter, in the course of a second sub-stage (I.2), subjected to a mixing intensity which is from 0.3 to 0.8 times as great as the mixing intensity in the first sub-stage (I.1) and is brought, within a period of from 0.2 to 20 minutes, from the crystallite melting point of the polyolefin (a) to a temperature which is from 3.degree. to 40.degree. C. above this, and, if appropriate, is immediately thereafter, in a third sub-stage (I.3), subjected to a mixing intensity which is from 0.5 to 1.0 times as great as the mixing intensity in the second sub-stage (I.2) and kept for a period of from 0.2 to 10 minutes at the temperature reached in sub-stage (I.2), and immediately thereafter, in a second stage (II), the mixture is discharged from the mixer within a period of from 0.5 to 30 seconds and is brought, within 120 seconds, to a temperature below the crystallite melting point of the polyolefin (a).