Selfbonded nonwoven fabrics
AssigneeFiber Industries, Inc.
InventorsHazael E. Booker, Barrie L. Davies, Alfred J. Hughes, Charles J. Shimalla
Life of this patent
Estimating the term…
Abstract
A selfbonded nonwoven fabric comprising at least 70 weight percent of sheath/core heterofilaments having a core of isotactic polypropylene in which the sheaths are high density polyethylene in an amount of 5 to 30 weight percent of the heterofilaments, and method of preparation. The fabrics have outstanding strength, fatigue resistance, and tear resistance and are eminently suitable for civil engineering applications such as unpaved road underlay material.
Claims4
An improved process for preparing a fabric having an Elmendorf tear strength (ASTM D-1424), T, of at least 6 lb. and a normalized grab tensile strength, G, of at least 120 lb. (ASTM D-1117) for a 140 gm/meter.sup.2 fabric, and the value of the product T.times.G being at least 1,200 by a process comprising the steps of melt spinning sheath/core heterofilaments, drawing the spun filaments, laying the drawn filaments to form an unbonded web, and thereafter bonding the web by the application of heat and pressure to form a selfbonded nonwoven fabric without using solvents that are relatively non-volatile at the bonding conditions, wherein the improvement comprises:
- (i) melt spinning sheath/core heterofilaments, wherein said sheath is high density polyethylene having a solid state density in the range from 0.930 to 0.965 gm/cc and having a melt flow index from 1 to 50 as measured by ASTM D-1238, and wherein said high density polyethylene comprises from 5 to 30 weight percent of said heterofilament;
- (ii) drawing said spun heterofilaments at a draw ratio within the range 2.0 to 6.0, at a temperature up to 120.degree. C.;
- and
- (iii) bonding said unbonded web at a temperature of from 120.degree. to 155.degree. C. at a nip stress in the range of 50 to 140 pounds per square inch, whereby said sheaths are softened.
Dependencies are inferred from the claim text.