Alumina ceramic
AssigneeGeneral Electric Company
InventorsRichard J. Charles, Svante Prochazka, Curtis E. Scott
Life of this patent
Estimating the term…
Abstract
A particulate dispersion of .alpha.-alumina, magnesium oxide and an additive selected from the group consisting of zirconium oxide, hafnium oxide and mixtures thereof, is formed into a green body and sintered in hydrogen producing a theoretically dense ceramic with improved optical transmission properties.
Claims14
A process for producing an optically translucent polycrystalline alumina sintered body which consists essentially of providing at least a substantially homogeneous dispersion consisting essentially of alumina, MgO or precursor therefor, and an additive selected from the group consisting of ZrO.sub.2, HfO.sub.2, and a mixture thereof or precursors therefor, said alumina ranging in composition from .alpha.-Al.sub.2 O.sub.3 to at least about 80% by weight .alpha.-Al.sub.2 O.sub.3 with the remaining alumina being of polymorphic form other than .alpha., said MgO being present in an amount ranging from about 0.03% by weight to less than about 0.15% by weight of said alumina, said ZrO.sub.2 being present in an amount ranging from higher than 0.002% by weight up to about 0.07% by weight of said alumina, said HfO.sub.2 being present in an amount ranging from higher than 0.003% by weight up to about 0.12% by weight of said alumina, said mixture of ZrO.sub.2 and HfO.sub.2 being composed of all ratios of ZrO.sub.2 and HfO.sub. 2 and being present in a total amount ranging from higher than 0.002% by weight up to about 0.12% by weight of said alumina, said dispersion having an average crystalline size ranging from about 0.05 micron to less than one micron, forming said dispersion into a green body having a density of at least about 30% of the theoretical density of 3.98 g/cc for alumina, and sintering said body in an atmospheric of hydrogen having a dew point higher than +30.degree. C. at a sintering temperature ranging from about 1750.degree. C. to about 1950.degree. C. producing a sintered body of theoretical density based on the density of 3.98 g/cc for alumina, said precursor decomposing completely below said sintering temperature to form said oxide and by-product gas.
An optically translucent polycrystalline alumina sintered body of theoretical density based on the density of 3.98 g/cc for alumina consisting essentially of alumina, magnesium and a component selected from the group consisting of zirconium, hafnium and a mixture thereof, said magnesium being present in an amount equivalent to from about 0.03% MgO by weight to less than about 0.15% MgO by weight of said sintered body, said zirconium being present in an amount equivalent to from higher than about 0.002% ZrO.sub.2 by weight up to about 0.07% ZrO.sub.2 by weight of said sintered body, said hafnium being present in an amount equivalent to from higher than about 0.003% HfO.sub.2 by weight up to about 0.12% HfO.sub.2 by weight of said sintered body, said mixture thereof being composed of all ratios of said zirconium and hafnium and being present in an amount equivalent to from higher than 0.002% of the di-oxides thereof by weight up to about 0.12% of the di-oxides thereof by weight of said sintered body, said sintered body ranging from a single phase to one composed of a primary phase and secondary phase ranging up to but less than 1% by volume of the total volume of said sintered body, said sintered body having an average grain size ranging from about 15 microns to about 100 microns.
An optically translucent polycrystalline alumina sintered body of theoretical density based on the density of 3.98 g/cc for alumina consisting essentially of .alpha.-Al.sub.2 O.sub.3, magnesium and zirconium, said magnesium being equivalent to about 0.03% MgO by weight to about 0.05% MgO by weight of said sintered body, said zirconium being equivalent to from about 0.01% ZrO.sub.2 by weight to about 0.04% ZrO.sub.2 by weight of said sintered body, said sintered body ranging from a single phase to one composed of a primary phase and secondary phase ranging up to but less than 1% by volume of the total volume of said sintered body, said sintered body having an average grain size ranging from about 20 microns to about 50 microns.
An optically translucent polycrystalline alumina sintered body of theoretical density based on the density of 3.98 g/cc for alumina consisting essentially of .alpha.-Al.sub.2 O.sub.3, magnesium and hafnium, said magnesium being equivalent to about 0.03% MgO by weight to about 0.05% MgO by weight of said sintered body, said hafnium being equivalent to from about 0.01% HfO.sub.2 by weight to about 0.07% HfO.sub.2 by weight of said sintered body, said sintered body ranging from a single phase to one composed of a primary phase and secondary phase ranging up to but less than 1% by volume of the total volume of said sintered body, said sintered body having an average grain size ranging from about 20 microns to about 50 microns.
An optically translucent polycrystalline sintered alumina body of theoretical density based on the density of 3.98 g/cc for alumina consisting essentially of .alpha.-Al.sub.2 O.sub.3, magnesium, zirconium and hafnium, said magnesium being equivalent to about 0.03% by weight to about 0.05% MgO by weight of said sintered body, the total amount of said zirconium and hafnium being equivalent to from about 0.01% of the di-oxides thereof by weight to about 0.07% of the di-oxides thereof by weight of said sintered body, said sintered body ranging from a single phase to one composed of a primary phase and secondary phase ranging up to but less than 1% by volume of the total volume of said sintered body, said sintered body having an average grain size ranging from about 20 microns to about 50 microns.
Dependencies are inferred from the claim text.