A stock material for producing seamless containers from a black plate base includes applying a layer of insoluble crystalline phosphate to each surface of the black plate and subsequently producing a thin film of organic lubricating material on the exposed surfaces of the phosphate layers so that a drawn and ironed container can be produced from a flat blank without the use of any additional lubricants during fabrication. The weight of the phosphate layer for each surface of the black plate base is preferably less than 100 milligrams per square foot, while the weight of lubricating film is on the order of 70 to 360 milligrams per square foot. In the preferred embodiment, the phosphate layer is preferably in the range of 20 to 35 milligrams per square foot, and the lubricant layer is on the order of 70 to 180 milligrams per square foot.
A method for treating metal surfaces of a thin metal sheet to form a coating suitable for use in multi-stage ironing operations to reduce the thickness of said sheet comprising contacting at least one metal surface with an aqueous phosphate solution to produce a totally reacted layer of insoluble crystalline phosphate containing iron phosphate and having a thickness equivalent of less than 100 milligrams per square foot with said phosphate layer having a grain size in the range of about 400 to about 2,500 angstroms, rinsing and cleaning the surface of the phosphate layer to remove all unreacted phosphate, and applying an organic ester lubricant non-reactive with said phosphate to said surface in an amount no greater than 425 milligrams per square foot.
In the method of forming seamless containers from a black plate stock material in which blanks are cut from said black plate stock material and said discs are thereafter first formed into cups and then subjected to at least one ironing step in the presence of a lubricant, the improvement of contacting a surface of stock material with an aqueous acidic phosphate solution to produce a layer of insoluble crystalline phosphate containing iron phosphate chemically bonded to the stock material surface in an amount of less than 100 milligrams per square foot and having a grain size of about 400 to about 2,500 angstroms, contacting the surface of the insoluble crystalline phosphate layer with an organic ester lubricant to produce a layer of said lubricant on said phosphate layer and in an amount no greater than about 425 milligrams per square food and thereafter performing said forming and ironing steps.