Supported vanadia catalyst and use thereof for nitrile production
AssigneeThe Lummus Company
InventorMorgan C. Sze
Life of this patent
Estimating the term…
Abstract
Vanadia supported on a silica-alumina or gamma-alumina support in an amount to provide a vanadia to support weight ratio ranging from about 0.3:1 to about 3:1 substantially entirely within the pores of the support, the vanadia having been placed in molten form substantially within the pores of a support having a surface area greater than about 50 m.sup.2 gram, a porosity greater than about 0.4 cc/gram which further includes an alkali metal, with the vanadium metal to alkali metal mole ratio being from 2:1 to 30:1. At least a portion of the alkali metal is preferably in the form of alkali metal vanadate. The catalyst is used for the production of nitriles from a compound containing at least one alkyl group.
Claims24
In a process for producing a nitrile by the catalytic ammoxidation of a compound containing at least one alkyl group convertible to a nitrile group by reaction with ammonia in the presence or absence of gaseous oxygen, the improvement comprising:
- effecting said ammoxidation with a catalyst comprising vanadia supported on a porous support in an amount to provide a vanadia to support weight ratio ranging from about 0.3:1 to about 3:1 substantially entirely within the pores of the support, said vanadia having been placed in molten form substantially within the pores of a support having a surface area greater than about 50 m.sup.2 per gram, a porosity greater than about 0.4 cc per gram, said catalyst containing an alkali metal in an amount to provide a vanadia metal to alkali metal mole ratio of from 2:1 to 30:1.
In a process for producing a nitrile by the catalytic ammoxidation of a compound containing at least one alkyl group convertible to a nitrile group by reaction with ammonia in the presence or absence of gaseous oxygen, the improvement comprising:
- effecting said ammoxidation with a catalyst produced by heating a mixture of an alkali metal hydroxide and vanadia supported on a porous support having a surface area greater than about 50 meters square per gram and a porosity greater than about 0.4 cc per gram to the fusion temperature of vanadia at an average rate of less than 20.degree. F. per minute, said vanadia and alkali metal hydroxide being employed in an amount to provide a vanadia to support weight ratio of from 0.3:1 to 3:1 substantially within the pores of the support and a vanadia metal to alkali metal mole ratio of from about 2:1 to 30:1, and maintaining the support mixture at vanadia fusion temperature to place the vanadia substantially entirely within the pores of the support.
Dependencies are inferred from the claim text.