Method for applying lubricants onto metal working surfaces
AssigneeAluminum Company of America
InventorRichard P. Kole
Life of this patent
Estimating the term…
Abstract
A method is disclosed for applying an ordinarily high viscosity lubricant as an atomized spray onto metal working surfaces without the use of high velocity air. The method comprises the steps of heating the lubricant to a temperature of approximately 170.degree. to 300.degree. F., hydraulically atomizing the lubricant by feeding the lubricant through a nozzle under a pressure of approximately 30 to 70 pounds per square inch whereby the relative velocity of the lubricant with respect to ambient atmosphere is increased upon exiting an orifice in the nozzle, and directing the lubricant onto the metal working surfaces.
Claims5
A method of uniformly spraying an ordinarily high viscosity nonaqueous lubricant containing solid additives onto the metal working surfaces of heated dies in a forging press comprising the steps of:
- heating said lubricant to approximately 170.degree. to 300.degree. F. to reduce its viscosity to approximately 1.0 centipoise;
- continuously recirculating a constant volume of said lubricant at a pressure of approximately 30 to 70 pounds per square inch and a temperature of approximately 170.degree. to 300.degree. F. from the source of heat to a spray nozzle;
- hydraulically atomizing said recirculating lubricant by selectively feedng said lubricant through said nozzle under said pressure;
- and
- directing said atomized lubricant onto said metal working surfaces.
A method of applying an ordinarily high viscosity, petroleum based, nonaqueous liquid lubricant containing solid additives with a viscosity of from approximately 300 to 2000 centipoise at 104.degree. F. onto the metal working surfaces of heated dies of a forging press comprising the steps of:
- heating said lubricnt to a temperature of approximately 170.degree. to 330.degree. F., such that the viscosity of said lubricant approximates that of water at standard temperature and pressure;
- continuously recirculating a substantially constant volume of said lubricant from the source of heat to a spray nozzle at a pressure of approximately 30 to 70 pounds per square inch;
- hydraulically atomizing said lubricant by feeding said lubricant through said nozzle solely under said pressure of approximately 30 to 70 pounds per square inch;
- and
- directing a uniform layer of said lubricant spray onto said metal working surfaces of said forging dies.
Dependencies are inferred from the claim text.