Methanation catalysts and process for their preparation
AssigneeUnion Oil Company of California
InventorsHoward D. Simpson, Hugh W. Gowdy, Steven D. Light
Life of this patent
Estimating the term…
Abstract
Methanation catalysts and process for preparing and using the same are disclosed; said methanation catalysts being especially suitable for producing synthetic fuel gas, from either naturally occurring liquid hydrocarbons or synthetic liquid hydrocarbons produced from solid carbonaceous materials, the product gas having substantially the same heating value and density as natural gas and which may be intermingled therewith and distributed through the same pipe lines. The methanation catalyst comprises an interspersed mixture of metals selected from Groups IV(B), V(B), VI(B) and VIII metals of the Periodic Table, composited with an inorganic refractory oxide support or matrix.
Claims19
A methanation catalyst suitable for use in the synthesis of synthetic fuel gas from liquid hydrocarbons, said methanation catalyst comprising an interspersed mixture of metals selected from Groups IV(B), V(B), or VI(B), in combination with two Group VIII metals, composited with an inorganic refractory oxide support or matrix;
- said methanation catalyst having an average pore diameter of from about 60 A to about 400 A;
- a surface area ranging from about 50 M.sup.2 /g to about 500 M.sup.2 /g;
- a pore volume of from about 0.2 cc/g to about 0.8 cc/g;
- a compacted bulk density of from about 0.6 to about 1.2;
- and wherein said catalyst comprises either Group IV(B), V(B) or VI(B) metals or a mixture thereof;
- combined with two Group VIII metals;
- and an inorganic refractory oxide support or matrix in a molar ratio range of from about 10:20:70 to about 1:1:98.
A methanation catalyst suitable for use in the synthesis of synthetic fuel gas from liquid hydrocarbon, said methanation catalyst comprising an interspersed mixture of chromium, nickel and platinum, composited with alumina;
- said methanation catalyst having an average pore diameter of from about 60 A to about 400 A;
- a surface area ranging from about 50 M.sup.2 /g to about 500 M.sup.2 /g;
- a pore volume of from about 0.2 cc/g to about 0.8 cc/g;
- a compacted bulk density of from about 0.6 to about 1.2;
- and wherein said catalyst comprises chromium;
- nickel and platinum;
- and alumina in a molar ratio range of from about 10:20:70 to about 1:1:98.
A process for preparing a methanation catalyst suitable for use in the synthesis of synthetic fuel gas from liquid hydrocarbons comprising forming a mixture by impregnating an inorganic refractory oxide support or matrix with a solution of a Group VIII metal compound, drying and calcining the resultant mixture, impregnating the mixture with either a solution of a Group IV(B), V(B), or VI(B) metal compound in combination with a solution of a second Group VIII metal compound, and, drying the resultant catalyst.
A process for preparing a methanation catalyst suitable for use in the synthesis of synthetic fuel gas from liquid hydrocarbons comprising, forming a mixture by impregnating alumina with a solution of a nickel compound;
- drying and calcining the resultant mixture;
- impregnating the mixture with a solution of a chromium compound and platinum compound;
- drying the resultant catalyst;
- and, alternatively, calcining the resultant catalyst.
Dependencies are inferred from the claim text.