Synthetic CO.sub.2 acceptor
AssigneeConoco Inc.
InventorsMichael S. Lancet, George P. Curran
Life of this patent
Estimating the term…
Abstract
A synthetic CO.sub.2 acceptor consisting essentially of at least one compound selected from the group consisting of calcium oxide and calcium carbonate supported in a refractory carrier matrix, the carrier having the general formula Ca.sub.5 (SiO.sub.4).sub.2 CO.sub.3. A method for producing the synthetic CO.sub.2 acceptor is also disclosed.
Claims5
A synthetic CO.sub.2 acceptor consisting essentially of at least one calcium compound selected from the group consisting of calcium oxide and calcium carbonate supported in a refractory carrier matrix, said carrier having the general formula Ca.sub.5 (SiO.sub.4).sub.2 CO.sub.3, wherein said calcium compound is present in an amount up to about 50 weight percent, calculated as calcium oxide, based on the weight of the acceptor.
A method for producing a synthetic CO.sub.2 acceptor, said acceptor comprising a mixture of calcium carbonate and spurrite, Ca.sub.5 (SiO.sub.4).sub.2 CO.sub.3 said method consisting essentially of:
- (a) mixing calcium carbonate, silica and water to produce a pelletizable mixture containing from about 85 to about 90 weight percent calcium carbonate and from about 10 to about 15 weight percent silica;
- (b) pelletizing said mixture to produce particles of a desired size;
- and
- (c) heating said particles to a temperature of at least 1500.degree. F. for at least 30 minutes at a steam pressure of at least about 18 atmospheres and a carbon dioxide pressure of at least 2 atmospheres to produce said synthetic CO.sub.2 acceptor.