Porous body of aluminum or its alloy and a manufacturing method thereof
AssigneeNippon Dia Clevite Co., Ltd.
InventorsToru Morimoto, Tsuyoshi Ohsaki, Toshio Ohkawa, Kenji Matsuzawa
Life of this patent
Estimating the term…
Abstract
A porous sintered material of good permeability and effective sound absorbability, being formed by combining between particles of aluminum or aluminum alloy powder into a body by means of sintering and having connecting pores among the particles of said aluminum or aluminum alloy powder. Said porous sintered material is obtained by mixing aluminum or an aluminum alloy with a low melting point aluminum alloy, forming the mixture into the predetermined shape and sintering it at a temperature which is at least 10.degree. C. lower than the melting point of the base material and higher than that of the low melting point material.
Claims11
A porous body having excellent sound absorbing properties composed of a sintered body of stick-shaped, needle-shaped, oval-shaped or other irregular-shaped particles of a base material of aluminum or aluminum alloy powder and a second material of alumium alloy powder having a melting point at least 10.degree. C. lower than the melting point of said base material, said porous body having a network of connecting pores communicating with the surface of said body with a pore ratio of 33 to 50% of the total volume of the body.
A method of manufacturing a porous body comprising the steps of mixing a base material of powder and/or granular aluminum or aluminum alloy with a second material of powder and/or granular aluminum alloy, the melting point of said second material being at least 10.degree. C. lower than that of the base material, forming the mixture into a predetermined shape under a pressure of 0.8.times.10.sup.-3 kg/cm.sup.2 or less, and sintering said mixture in a nonoxidizing or inert atmosphere at a temperature which is at least 10.degree. C. lower than the melting point of the base material and is higher than the melting point of the second material.