Process for manufacture of stable sodium dithionite slurries
AssigneeVirginia Chemicals Inc.
InventorLeonard C. Ellis
Life of this patent
Estimating the term…
Abstract
Substantially stable slurries containing 30-35% by weight of sodium dithionite are manufactured by evaporating sodium dithionite solutions while maintaining the heating medium at 220.degree.-250.degree. F. and the solution and slurry at 110.degree.-155.degree. F. under a vacuum of at least 25 inches Hg and by promptly cooling the resultant slurry while agitating it. The vacuum is preferably 26.5-27.5 in. Hg. At 4-5% by weight of the sodium dithionite and preferably at 4.3% by weight, NaOH is preferably added to the solution or alternatively to the slurry, immediately after evaporation. A chelator is preferably added to the solution to prevent metal contamination thereof. Zinc-derived sodiation liquor is the preferred sodium dithionite solution.
Claims9
A process for producing a substantially stable sodium dithionite slurry having a sodium dithionite content of 25-45%, comprising:
- A. evaporating a sodium dithionite solution in an evaporator or crystallizer under a vacuum of 25-30 inches Hg, a steam heating jacket temperature of 220.degree.-250.degree. F., and a slurry temperature of 110.degree.-155.degree. F. to create a hot slurry;
- and
- B. cooling said hot slurry promptly while under agitation to create said stable slurry, wherein NaOH is either added to said solution before said evaporating or added immediately following said evaporating of said solution in an amount of 4-5% by weight of said sodium dithionite.
Dependencies are inferred from the claim text.