Method for removing aluminide coatings from nickel or cobalt base alloys
AssigneeROLLS-ROYCE plc
InventorFrank Cork
Life of this patent
Estimating the term…
Abstract
A method of removing aluminium containing alloy coatings from nickel or cobalt base alloy substrates in which the coated substrate is immersed in an aqueous mixture of nitric and sulphamic acids until coating dissolution is complete. A solution containing 5 to 30% vol./vol. nitric acid and from 5 to 30% wt./vol. sulphamic acid is preferred.
Claims5
A method of removing an aluminum containing alloy coating from a nickel or cobalt base alloy substrate comprising immersing the coated substrate in an aqueous mixture containing from about 5 to about 30% vol./vol. nitric acid and from about 5 to about 30% wt./vol. sulphamic acid.
A method of removing an aluminum containing alloy coating from a nickel or cobalt base alloy substrate while avoiding any substantial intergranular attack of said substrate, said method comprising
- (1) immersing the coated substrate in an aqueous mixture containing from about 5 to about 30% vol./vol. nitric acid and from about 5 to about 30% wt./vol. sulphamic acid, said mixture being maintained at between room temperature and 60.degree. C;
- (2) continuing said immersion until substantially all of the coating is dissolved from the substrate;
- and thereafter
- (3) removing the thus treated substrate from the aqueous mixture.