Direct method for production of high-grade, high-purity ferromanganese

A method for the production of high-grade, high-purity ferromanganese consisting of not less than 90% Mn, not more than 1.5% Si, not more than 0.1% C and not more than 0.05% P comprising the steps of charging a molten Mn-containing material having a Mn content in the range from 10 to 40%, at least one non-carbonaceous reducing agent selected from the group consisting of Si-containing alloys, Al-containing alloys and Ca-containing alloys and a slagging material in a reaction vessel capable of performing horizontal eccentric circular motion and subjecting the reaction vessel to the said horizontal eccentric circular motion at between 35 and 65 cycles per minute to mix and agitate the contents of the vessel, whereby the Mn oxide contained in the molten Mn-containing material is reduced by the non-carbonaceous reducing agent.