Dental prostheses
AssigneePerdent, GmbH.
InventorsRudy Michl, Peter Wollwage
Life of this patent
Estimating the term…
Abstract
Dental prosthetic devices, such as artificial teeth, crowns, bridges and replacements for parts of teeth are provided comprising hardened resin dental materials containing at least one polymer and a finely divided inorganic filler, said filler being present in an amount of about 10 to 90% based on the weight of the material and having a particle size within the range of 10 to 400 millimicrons, said materials having an extremely high compressive strength, clear opalescence and a very smooth homogeneous surface.
Claims17
A dental prosthesis having clear opalescence, resistance to abrasion and capable of being polished, comprising a hardened composition, comprising:
- a first component comprising a monomeric binding material selected from a member of the group consisting of (a) long chain monomer esters of bisphenol A and glycidyl methacrylates, (b) adducts of diisocyanates and hydroxymethylacrylates, (c) difunctional esters of acrylic and methacrylic acids, and (d) mixtures of two, or of three of (a), (b) and (c), and
- a second component comprising a micro-fine inorganic filler being present in an amount of about 50 to 90% based on the weight of said composition and having a particle size within the range of about 10 to 400 millimicrons and a BET surface area of less than about 200 m.sup.2 /g, wherein at least 50% of the filler particles have a particle size within the range of 10 to 40 millimicrons, in admixture with at least one bead or chip polymer of the group consisting of polyvinylchloride and copolymers thereof, polystyrene and copolymers thereof, polyamides, polymeric acrylates and polymeric methacrylates.
A method of making a dental prosthesis, comprising:
- a. forming a composition comprising:
- a first component comprising a monomeric binding material selected from a member of the group consisting of (a) long chain monomer esters of bisphenol A and glycidyl methacrylates, (b) adducts of diisocyanates and hydroxymethylacrylates, (c) difunctional esters of acrylic and methacrylic acids, and (d) mixtures of two, or of three of (a), (b) and (c), and
- a second component comprising a micro-fine inorganic filler being present in an amount of about 50 to 90% based on the weight of said composition and having a particle size within the range of about 10 to 400 millimicrons and a BET surface area of less than about 200 m.sup.2 /g, wherein at least 50% of the filler particles have a particle size within the range of 10 to 40 millimicrons, in admixture with at least one bead or chip polymer of the group consisting of polyvinyl chloride and copolymers thereof, polystyrene and copolymers thereof, polyamides, polymeric acrylates and polymeric methacrylates,
- b. molding said composition into an appropriate shape for making said dental prosthesis, and
- c. polymerizing said molded composition.