Electrical contact material
AssigneeNippon Telegraph & Telephone Public Corporation
InventorsKoichi Fujiwara, Coro Yamauchi, Kishio Arita, Shigeyuki Tsurumi
Life of this patent
Estimating the term…
Abstract
An electrical contact material and method of producing the same are provided. The material is an internally oxidized silver eutectic alloy system with a main component of silver to which at least one of silicon and germanium is added and, for characteristic improvement purpose, at least one selected from at least one of the groups consisting respectively of gold, platinum and the like, titanium, rhenium and the like, and iron, cobalt and the like is further added. In producing the material, an ingot of said alloy is hot-worked and then internally oxidized at a temperature in a range from 250.degree. C. to the eutectic temperature of the alloy.
Claims5
An electrical contact material comprising a silver eutectic alloy comprising Ag as the main component and an additive comprising:
- (a) at least one element selected from the group consisting of Si and Ge in an amount of 1 to 17 at.%;
- and
- (b) at least one element selected from the group consisting of Au, Pt, Pd, Rh, Ru, Os and Ir in an amount of 1 to 10 at.%.
- said elements being in the form of fine crystals uniformly dispersed in said Ag and internally oxidized and said at.% based on the weight of the material.
An electrical contact material comprising a silver eutectic alloy comprising Ag as the main component and an additive comprising:
- (a) at least one element selected from the group consisting of Si and Ge in an amount of 1 to 17% at.%;
- and
- (b) at least one element selected from the group consisting of Ti, V, Zr, Nb, Mo, Ta, W, and Re in an amount of 1 to 5 at.%.
- said elements being in the form of fine crystals uniformly dispersed in said Ag and internally oxidized and said at.% based on the weight of the material.
An electrical contact material comprising a silver eutectic alloy comprising Ag as the main component and an additive comprising:
- (a) at least one element selected from the group consisting of Si and Ge in an amount of 1 to 17 at.%;
- and
- (b) at least one element selected from the group consisting of Fe, Co, Ni and Cu in an amount of 1 to 5 at.%;
- said elements being in the form of fine crystals uniformly dispersed in said Ag and internally oxidized and said at.% based on the weight of the material.
Dependencies are inferred from the claim text.