Loading patent…
AssigneeVianova Kunstharz, A.G.
InventorsGerhard Schmolzer, Wolfgang Daimer, Heiner Verdino
Estimating the term…
Cathodically depositable paint binders, water-soluble upon neutralization with acids, and the method of preparing the paint binders based on amine-epoxy adducts which crosslink at elevated temperature through polyurethane formation are described. The paint binders are prepared by reacting per mole of expoxide groups of a polymer having an epoxy equivalent of between about 180 and 1500 from about 3 to 70 mole percent of a polyisocyanate adduct having substantially no free NCO content and carrying per molecule at least one carboxyl group. Basic functionality is provided by reacting the epoxy-containing polymer, before or after reaction with the polyisocyanate adduct, with secondary aliphatic amines and/or alkanol amines. The binders, in addition to providing stable aqueous solutions when neutralized with an inorganic or organic acid, have good resistance to corrosion and solvents.
Cathodically depositable paint binders water-soluble upon neutralization with acids comprising the reaction product of a polymer having an epoxy equivalent of between about 180 and 1500 with from about 3 to 70 mole percent per mole of epoxy groups on said polymer of a polyisocyanate adduct having substantially no free NCO content and carrying per molecule at least one carboxyl group, said epoxy containing polymer having basic functionality sufficient to solubilize said binder in water upon neutralization with an acid, said basic functionality provided in said polymer through reaction of said epoxy containing polymer with a secondary aliphatic amine or alkanol amine, said reaction product having an acid value of below about 5 mg KOH/g and an amine value of from about 24 to 150 mg KOH/g.
An aqueous solution of a cathodically depositable paint binder obtained through the neutralization reaction with an acid of the reaction product of a polymer having an epoxy equivalent of between about 180 and 1500 with from about 3 to 70 mole percent per mole of epoxy groups on said polymer of a polyisocyanate adduct having substantially no free NCO content and carrying per molecule at least one carboxyl group, the basic functionality for neutralization provided in said polymer through reaction of the said epoxy containing polymer with a secondary aliphatic amine or alkanol amine, said water-soluble binder having an acid value of below about 5 mg KOH/g and an amine value of from about 24 to 150 mg KOH/g.
The process for producing paint binders soluble upon neutralization with organic or inorganic acids comprising the steps of reacting at a temperature of from about 80.degree. to 160.degree. C. an epoxy group containing polymer having an epoxy equivalent of between about 180 and 1500 with from about 3 to 70 mole percent per mole of epoxy groups on said polymer of a polyisocyanate adduct having substantially no free NCO content and carrying per molecule at least one carboxyl group, and providing basic functionality on said epoxy group containing polymer by reacting epoxy groups on said epoxy containing polymer with a secondary aliphatic amine or alkanol amine at from 20.degree. to 150.degree. C., said reaction being continued until a maximum acid value of 5 mg KOH/g and an amine value of from 24 to 150 mg KOH/g is obtained.
Dependencies are inferred from the claim text.