Method of manufacture of optical fiber
AssigneeEotec Corporation
InventorDavid A. Krohn
Life of this patent
Estimating the term…
Abstract
A process is disclosed for manufacturing an optical fiber comprising a silica cladding and multi-component glass core wherein a tube made of the cladding material serves as a crucible in which the core glass is melted and fined. The core glass includes silicon dioxide, boron oxide, barium oxide or lead oxide (or a combination of both, and an alkali oxide). The materials are selected to provide a high numerical aperture, rapid melting and stability at the high temperatures required to draw the fiber. In accordance with a further feature of the invention, the batch material for the core is actually melted as it is falling to the bottom of the silica tube, thereby increasing the speed of melting and further facilitating outgassing of effluents.
Claims5
A process for making a low loss optical fiber having a numerical aperture in excess of about 0.4 and comprising a multi-component glass core within a cladding material, including the steps of:
- melting a glass core composition with a tube made of a high-purity fused silica, said core glass composition comprising by weight 27% to 42% silicon dioxide, 7% to 50% boron oxide, 5% to 51% of an oxide selected from the group consisting of lead oxide and barium oxide, and 5% to 30% of an alkali oxide selected from the group consisting of lithium oxide, sodium oxide and potassium oxide;
- fining the melted core glass within said glass tube at a temperature substantially in excess of the melting temperature of said glass core composition to enable uniform mixing of said core glass and silica;
- and
- drawing said tube and core glass into said optical fiber.
Dependencies are inferred from the claim text.