Process for producing metal powder
AssigneeThe International Nickel Company, Inc.
InventorsIan S. R. Clark, John K. Pargeter
Life of this patent
Estimating the term…
Abstract
The invention is directed to a process for producing metal powder through atomizing in which a molten metal stream is subjected to the influence of a plurality but correlated sets of atomization jets by virtue of which a disintegrating medium exits from the jets at a velocity of at least Mach No. 1, the medium from one set of jets being angled to strike the falling molten body at a point below and at an angle less than the medium dispensed from the other set of jets, whereby less flake and filigree are formed, a higher powder yield obtains, lower medium pressure can be used, etc.
Claims11
An atomization process for producing metal powder through gaseous disintegration of a molten stream in an atomizing tank using a controlled multiple impact mode system as herein defined and which by reason of such multiple impact mode, as opposed to an otherwise single impact mode, (i) powder loss through filigree formation (powder adherence to the interior wall of the atomizing tank) is minimized, (ii) powder loss through flake formation (powder deflecting from the interior tank wall) is reduced, (iii) a higher yield of metal powder is achieved, the foregoing being achievable (iv) though gas pressure and gas consumption be relatively low, which comprises,
- (a) directing molten metal in a downwardly stream through a venturi teeming nozzle at a rate of from about 10 to about 65 kg/min,
- (b) directing jets of gas through venturi jets to impinge against the molten metal stream to atomize said stream and thereby cool the stream such that droplets form,
- (c) said gas being delivered from the jets at an exit velocity of at least Mach. No. 1 such that a supersonic tongue of up to at least three inches is maintained and under a multiple impact mode system in which gas impinges against the stream at least twice at precisely determined but different locations using at least two groups of separate jets with a first group of jets being angled downwardly relative to the falling metal stream such that the gaseous medium dispensed therefrom at supersonic velocity strikes the molten metal at a first point downstream, and with at least a second group of downwardly angled jets arranged such that the gaseous medium dispensed therefrom at supersonic velocity strikes the metal at a second point downstream but below the said first point of impact and at an angle different from the first at least about 1.degree. less than the first angle of impact,
- (d) and thereafter further cooling the droplets formed to complete the powder formation process.
An atomization process for producing metal powder through disintegration of a molten stream in an atomizing tank using a controlled multiple impact mode system as herein defined and which by reason of such multiple impact mode as opposed to an otherwise single impact mode, (i) powder loss through filigree formation (powder adherence to the interior wall of the atomizing tank) is minimized, (ii) powder loss through flake formation (powder deflecting from the interior tank wall) is reduced, (iii) a higher yield of metal powder is achieved, which comprises,
- (a) directing molten metal in a downwardly stream through a teeming nozzle at a rate of from about 10 to about 65 kg/min,
- (b) directing jets of an atomizing fluid to impinge against the molten metal stream to atomize said stream and thereby cool the stream such that droplets form,
- (c) said atomizing fluid being delivered from the jets at an exit velocity of at least Mach No. 1 such that a supersonic tongue of up to at least three inches is maintained and under a multiple impact mode system in which atomizing fluid impinges against the stream at least twice at precisely determined but different locations using at least two groups of separate jets, with a first group of jets being angled downwardly relative to the falling metal stream such that the atomizing fluid dispensed therefrom at supersonic velocity strikes the molten metal at a first point downstream, and with at least a second group of downwardly angled jets arranged such that the atomizing fluid dispensed therefrom at supersonic velocity strikes the metal stream at a second point downstream but below the said first point of impact and at an angle different from the first at least about 1.degree. less than the first angle of impact,
- (d) and thereafter further cooling the droplets formed to complete the powder formation process.