US 4,270,977 AGranted

Process for preparing water sorptive products

AssigneeNL Industries, Inc.

InventorsDaniel F. Herman, Uno Kruse

Life of this patent

Estimating the term…

Loading patent…

Abstract

The present invention is directed to a process for preparing cellulose containing water sorptive products from an aqueous suspension or paper furnish in accordance with conventional paper making techniques. The suspension or paper furnish employed in preparing the sorptive products comprises a polymer component and a fibrous component slurried in water. The polymer component is provided from a specifically defined class of crosslinked copolymers which contain carboxyl groups. A representative polymer from this class includes that obtained by reacting methyl acrylate and methacrylate acid in the presence of ethylene glycol dimethacrylate. The polymer component becomes water sorptive when the carboxyl groups present thereon are neutralized with a base. In the practice of the process of the present invention, a composite product is prepared from the above mentioned suspension, partially dried, and then neutralized in a specifically controlled manner. Neutralization is achieved while controlling the amount of base and water which contacts the composite product. The control is exercised in a manner sufficient to achieve a proper degree of salting and to prevent undue sorption of the water during neutralization. Such control results in a substantial improvement in the cost efficiency of the process since the amount of water which must be eventually evaporated from the neutralized product is held to a minimum.

Claims9

Dependent claims

A process for preparing a water sorptive product which comprises:

(1) forming an aqueous suspension comprising a slurry of a potentially water swellable, water-insoluble polymer component and a fibrous component in water wherein the polymer component comprises the reaction product of:
(a) from about 15% to about 50% by weight of an olefinically-unsaturated carboxylic acid;
(b) from about 49.07% to about 82% by weight of an alkyl acrylate wherein the alkyl group has from 1 to 6 carbon atoms;
and
(c) from about 0.03% to about 3.0% by weight of a crosslinking agent, said reaction product having carboxyl groups present therein which when coverted to their salt form maintains the polymer water-insoluble and imparts the capability of said polymer component of sorbing water upon contact therewith;
and
wherein the fibrous component comprises at least 50% cellulose material, and the weight ratio of said polymer component to said fibrous component is controlled to from about 90:10 to about 5:95;
(2) forming a composite product from said suspension;
(3) partially drying said composite product to reduce the moisture content thereof to between about 3 and about 25%, by weight, based on the weight thereof;
(4) contacting said partially dried composite product with an amount of an aqueous solution of a base sufficient to achieve a degree of salting of the polymer component of said composite product of from about 100 to about 120% and thereby netralize the carboxylic groups present thereon and in a manner sufficient to prevent the weight ratio of the dry neutralized composite product to water sorbed therein from exceeding 1:10 without solubilizing the polymer salt;
and
(5) drying said neutralized composite product to reduce the moisture content thereof to not greater than about 25% by weight.

9 more elements

A process for preparing a composite sheet having water sorptive properties which comprises:

(1) depositing a suspension comprising a slurry of a polymer component and a fibrous component in water on a liquid permeable support to form a wet-laid web wherein said polymer component is a potentially water swellable, water-insoluble polymer comprises the reaction product of:
(a) from about 15% to about 50% by weight of an olefinically-unsaturated carboxylic acid;
(b) from about 49.07% to about 82% by weight of an alkyl acrylate wherein the alkyl group has from 1 to 6 carbon atoms;
and
(c) from about 0.03% to about 3.0% by weight of a crosslinking agent;
said reaction product having carboxyl groups present thereon which when converted to their salt form maintains the polymer water-insoluble and imparts the capability to said polymer component of sorbing water upon contact therewith;
and wherein said fibrous component comprises at least 50% by weight of cellulose fibers and the weight ratio of said polymer component to said fibrous component is controlled to be from about 90:10 to about 5:95;
(2) passing said wet-laid web through a drying zone wherein the moisture content is reduced to between about 3 and about 25% by weight thereof;
(3) passing said wet-laid web through a neutralizing zone wherein it is contacted with an aqueous alkaline solution containing a base in an amount sufficient to achieve a degree of salting of the polymer component of from about 100 to about 120% and thereby neutralize the carboxyl groups present thereon causing the polymer component to swell and increase in thickness from sorption of water without solubilizing the polymer salt;
(4) sensing the thickness of the neutralized wet-laid web as it exits the neutralizing zone;
(5) controlling the rate of travel of said wet-laid web through the neutralizing zone in response to the sensed wet-laid web thickness in a manner sufficient to prevent the weight ratio of the dry neutralized wet-laid web to water sorbed therein after exiting the neutralizing zone from exceeding 1:10;
(6) passing the neutralized wet-laid web through a drying zone wherein the moisture content thereof is controlled to be not greater than about 25% by weight.

9 more elements

Dependencies are inferred from the claim text.

Facts

Application: 06/090,207Filed 1 Nov 1979
Granted: 2 Jun 1981
Term ends: Not estimatedThe source records don’t support an estimate.

Classification11 codes

D21H 17/43
Anionic: carboxyl groups or derivatives thereof
A61L 15/60
Use of materials characterised by their function or physical properties: liquid-swellable gel-forming materials, e.g. super-absorbents
C08L 33/08
Of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical: homopolymers or…
D21F 11/14
Processes for making continuous lengths of paper, or of cardboard, or of wet web for fibre board production, on paper-making machines: making…