Method for easily removing zinc from carbon black contaminated with zinc
AssigneeTosco Corporation
InventorsFrank C. Haas, Manuel M. Gutierrez
Life of this patent
Estimating the term…
Abstract
The present invention relates to a method for removing zinc from solid carbon black, preferably obtained from the pyrolysis of rubber, said carbon black containing at least 3%, by weight, of zinc, calculated as ZnO, said method including the steps of contacting the carbon black at a temperature of at least 750.degree. C. with a gas selected from chlorine and hydrogen chloride to form gaseous zinc chloride from the zinc contained in said carbon black, and separating the gaseous zinc chloride from the solid carbon black.
Claims12
A method for purifying solid carbon black pellets without adversely affecting said pellets, said carbon black pellets being contaminated with at least 3%, by weight, of zinc, calculated as zinc oxide, which comprises forming carbon black pellets from very fine carbon black particles having an average diameter of less than about one micron and contaminated with at least 3%, by weight, of zinc, calculated as zinc oxide;
- contacting said carbon black pellets contaminated with zinc at a temperature of at least about 750.degree. C. with a non-aqueous gas selected from the group consisting of chlorine and hydrogen chloride thereby forming volatile zinc chloride, and separating the gaseous zinc chloride from the solid carbon black pellets.
A method for easily and economically removing zinc and sulfur from carbon black pellets without adversely affecting the pellets, said carbon black being contaminated with at least 3%, by weight, of zinc, calculated as zinc oxide and at least 1%, by weight, of sulfur, which comprises forming carbon black pellets from very fine carbon black particles having an average diameter of less than about one micron and contaminated with at least 3%, by weight, of zinc, calculated as zinc oxide and at least 1%, by weight, of sulfur;
- contacting said carbon black pellets at a temperature of between about 750.degree. C. to 1000.degree. C. with a non-aqueous gas selected from the group consisting of chlorine and hydrogen chloride thereby forming gaseous zinc chloride and sulfur chloride and separating the gaseous zinc chloride and the sulfur chloride from the carbon black pellets.