Method of producing glass optical filaments
AssigneeCorning Glass Works
InventorPeter C. Schultz
Life of this patent
Estimating the term…
Abstract
A method of incorporating an additive or dopant oxide into a glass body produced by the oxidation of vaporous source material in a flame. The resultant glassy particles are deposited to form a porous preform having a uniform refractive index. During the consolidation process, the preform is subjected to an atmosphere including a drying agent which penetrates the interstices of the soot preform to simultaneously dry and dope the preform.
Claims18
A method of forming a glass article comprising the steps of
- providing a tubular glass preform having an aperture therethrough, said preform having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform,
- disposing said preform in a furnace where it is heated to an elevated temperature,
- flowing into said preform aperture a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent, at least a portion of said stream flowing outwardly from the center of said preform through the interstices thereof to the outer surface thereof, said doping agent forming a dopant oxide, the concentration of which is greatest at the inner surface of said preform and which progressively decreases with increasing radius within said preform so that the refractive index within said preform is a maximum at the inner surface of said preform and decreases with increasing radius, and
- consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
A method of producing a light-conducting glass fiber having a refractive index distribution which progressively decreases from a maximum value at the axis thereof to a minimum value at some radius thereof, said method comprising
- providing a substantially cylindrical mandrel,
- depositing on said mandrel a coating of flame hydrolysis-produced glass soot to form a water-containing soot preform having a network of continuous open pores throughout its mass, the composition of said soot being substantially uniform throughout said preform,
- removing said mandrel to form a soot preform having an aperture therethrough,
- flowing into said preform aperture a stream of an atmosphere containing a drying agent and a doping agent for modifying the refractive index of said preform in such a manner that the refractive index of the inner portion of said preform is greater than that at the outer portion thereof, at least a portion of said stream flowing outwardly from the center of said preform through the interstices therein to the outer surface thereof, to simultaneously dope said preform and remove water therefrom,
- heating said preform to a temperature within the consolidation temperature range thereof for a time sufficient to cause said soot particles to fuse and form a dense glass article,
- heating said dense glass article to the drawing temperature thereof, and
- drawing said dense glass article to close said aperture and to reduce the cross-sectional area thereof, thereby forming an optical waveguide filament.
The method of claim 12 wherein said preform comprises glass particles doped with a dopant material to increase the refractive index thereof, said method further comprising the step of flowing along the outside of said preform a stream of a flushing atmosphere containing means to leach said dopant material from the outer portion of said preform.
A method of forming a glass article comprising the steps of
- providing an elongated tubular glass preform having an aperture therethrough and having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform,
- disposing said preform in a furnace where it is heated to an elevated temperature,
- subjecting the outer surface of said preform to an atmosphere containing a drying agent for removing water from said preform and an agent for modifying the refractive index of said preform in such a manner that the refractive index of the inner portion of said preform is greater than that at the outer portion thereof,
- reducing the pressure within said preform aperture to a value lower than that at the outside surface thereof, so that said atmosphere flows radially inwardly through said preform, and
- consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
A method of forming a glass article comprising the steps of
- providing an elongated tubular glass preform having an aperture therethrough and having a network of continuous open pores throughout its mass, the composition throughout said preform being substantially uniform,
- disposing said preform in a furnace where it is heated to an elevated temperature,
- flowing radially outwardly through the interstices of said preform a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent for increasing the refractive index at the inner portion of said preform,
- flowing radially inwardly through said preform a stream of an atmosphere containing a drying agent for removing water from said preform and a doping agent for lowering the refractive index at the outer portion of said preform, and
- consolidating said preform to form a tubular, dense glass body having a gradient refractive index.
Dependencies are inferred from the claim text.