Back to results
US 4,247,661 AGranted
Thermoplastic polymer blends comprising EP or EPDM polymers and highly crystalline polyallomers
AssigneeThe B. F. Goodrich Company
InventorsRichard M. Herman, Martin Batiuk
Life of this patent
Estimating the term…
Abstract
Certain thermoplastic blends have substantially improved hot strength (i.e., cohesive strength and resistance to sagging or tearing during milling or other hot processing). The blends comprise (1) at least one ethylene-propylene (EP) or ethylene-propylene-diene (EPDM) polymer and (2) at least one highly crystalline polyallomer, and are useful for tubing, wire and cable insulation, molded items and the like.
Claims7
A polymer blend having excellent hot strength comprising
- (1) A major proportion of at least one EP polymer consisting essentially of interpolymerized units of about 63 weight percent to about 85 weight percent ethylene and about 15 weight percent to about 37 weight percent propylene, or at least one EPDM polymer consisting essentially of interpolymerized units of about 63 weight percent to about 85 weight percent ethylene, about 5 weight percent to about 36.8 weight percent propylene, and about 15 weight percent of a diene monomer, said polymers having unstretched crystallinity from about 1% to about 25% and melt endotherms from about 1 to about 15 calories/gm, and
- (2) at least one polyallomer having at least 70 percent crystallinity (determined by solubility in refluxing hexane) and consisting essentially of interpolymerized units of (2) straight and branched chain aliphatic alpha-monoolefins containing 3 to 10 carbon atoms and (b) from about 1 to about 20 weight percent ethylene.
A polymer blend having excellent hot strength comprising
- (1) 100 weight parts of at least one EP polymer consisting essentially of interpolymerized units of about 63 weight percent to about 85 weight percent ethylene and about 15 weight percent to about 37 weight percent propylene, or at least one EPDM polymer consisting essentially of interpolymerized units of about 63 weight percent to about 85 weight percent ethylene, about 5 weight percent of a diene monomer, said polymers having unstretched crystallinity from about 1% to about 25% and melt endotherms from about 1 to about 15 calories/gm, and
- (2) at least about 5 to 99 weight parts of at least one polyallomer having at least 70 percent crystallinity (determined by solubility in refluxing hexane) and consisting essentially of interpolymerized units of (a) straight chain and branched chain aliphatic alpha-monoolefins containing 3 to 10 carbon atoms and (b) from about 1 to about 20 weight percent ethylene.
Dependencies are inferred from the claim text.