Process for the use of vinyl acetate-ethylene copolymer emulsions to adhere fibers to carpet backing
AssigneeAir Products and Chemicals, Inc.
InventorJohn G. Iacoviello
Life of this patent
Estimating the term…
Abstract
Use of vinyl acetate-ethylene copolymer emulsions as laminating adhesives for rug backing is disclosed. The copolymer emulsions are prepared by admixing vinyl acetate-ethylene copolymer, dispersant and thickening agent together, with or without the addition of filler. The vinyl acetate-ethylene copolymer can contain between about 20 and about 70 parts by weight of vinyl acetate and between about 30 and about 80 parts by weight of ethylene. The resulting vinyl acetate-ethylene copolymer emulsions have a glass transition temperature (T.sub.g) of between about -35.degree. C. and about -10.degree. C.
Claims7
The process for adhering fibers to carpet backing which comprises applying a polymeric emulsion containing as the only adhesive polymeric component a vinyl acetate-ethylene copolymer consisting of between about 61 and about 68 parts by weight of vinyl acetate per hundred parts of said copolymer, between about 32 and about 38 parts by weight of ethylene per hundred parts of said copolymer and up to about 0.7 parts by weight of another monomer selected from the group consisting of maleic acid, triallyl cyanurate and mixtures thereof per hundred parts of said copolymer;
- a dispersant in an amount between about 0.1 part and about 3 parts per hundred parts of said copolymer;
- and a thickening agent in an amount between 0.1 part and about 4 parts per hundred parts of said copolymer to the carpet backing material, removing excess polymeric emulsion and drying the emulsion thereby causing the fibers to adhere to the carpet backing material;
- said emulsion having a glass transition temperature of between about -35.degree. C. and about -10.degree. C.
In the process of structuring rugs and carpets by adhering pile material to at least one backing substrate with an adhesive, the improvement comprising using as the adhesive a polymeric latex containing:
- (1) as the only adhesive polymeric component a vinyl acetate-ethylene copolymer consisting of between 61 and 68 parts by weight of vinyl acetate per hundred parts of said copolymer, between 38 and 32 parts by weight of ethylene per hundred parts of said copolymer and up to about 0.7 parts by weight of another monomer selected from the group consiting of maleic acid, triallyl cyanurate and mixtures thereof per hundred parts of said copolymer;
- (2) a dispersant in an amount between about 0.1 part and about 3 parts by weight per hundred parts by weight of said copolymer;
- (3) a thickening agent in an amount between about 0.1 part and about 4 parts by weight per hundred parts by weight of said copolymer;
- and
- (4) a filler in an amount from 0 to about 500 parts by weight per hundred parts by weight of said copolymer;
- said adhesive having a glass transition temperature of between about -35.degree. C. and about -10.degree. C.