Process for manufacturing gypsum board
AssigneeUnited States Gypsum Company
InventorRichard F. Stone
Life of this patent
Estimating the term…
Abstract
A process and apparatus for producing a healed stucco having lowered water demand without loss of normal strength development potential which comprises, while blending a small amount of water with the calcined gypsum, simultaneously or substantially simultaneously grinding the calcined gypsum so as to increase the surface area of the calcined gypsum particles while incorporating about 1-10% by weight of the calcined gypsum of free water.
Claims6
An improved process for manufacturing gypsum board characterized by using a reduced amount of water to fluidize calcined gypsum in forming a gypsum slurry which is fed to a boardmaking machine while maintaining the compressive strength of the dried gypsum board which comprises:
- (1) Supplying calcined gypsum feed to be conveyed to a gypsum slurry mixer;
- (2) conveying the calcined gypsum feed to an impacting blender;
- (3) blending a small amount of water with said calcined gypsum and simultaneously or substantially simultaneously grinding the calcined gypsum to increase the surface area of the gypsum particles, said water ranging from about 1% to 10% by weight of the calcined gypsum feed, said grinding increasing the surface area of the gypsum particles up to about 4 times;
- (4) allowing the freshly exposed facets of the treated calcined gypsum particles to heal;
- (5) conveying the healed calcined gypsum to a gypsum slurry mixer;
- (6) adding additional water to the healed calcined gypsum in the slurry mixer, said additional water being added in an amount sufficient to provide from about 50 to 85 parts of water, including water added in the blender, per 100 parts of the calcined gypsum, which results in a substantially reduced amount of water to be evaporated from the wet boards;
- (7) mixing the healed calcined gypsum and water in the slurry mixer to form a homogeneous slurry;
- (8) feeding the slurry to a gypsum board making machine to form a wet gypsum board;
- (9) passing the wet gypsum board through a kiln to dry the board;
- (10) recovering dry gypsum board consisting essentially of calcium sulphate dihydrate.
An improved process for preparing calcined gypsum characterized by providing the calcined gypsum with a reduced water demand while maintaining its ability to develop the necessary compressive strength for a cast gypsum product which comprises;
- (1) supplying calcined gypsum feed to be conveyed to an impacting blender;
- (2) conveying the calcined gypsum feed into the blender;
- (3) blending a small amount of water with said calcined gypsum simultaneously or substantially simultaneously in the blender while grinding the calcined gypsum to increase the surface area of the calcined gypsum particles, said water ranging from about 1% to about 10% by weight of the calcined gypsum feed and said grinding increasing the surface area up to about 4 times the surface area of the untreated calcined gypsum feed;
- (4) allowing the freshly exposed facets of the treated and ground calcined gypsum particles to heal;
- (5) drying the healed calcined gypsum by subjecting it to elevated temperatures;
- (6) recovering a dried, healed calcined gypsum which is storage stable, has reduced water demand and is capable of developing substantially full compressive strength in a cast gypsum product.
Dependencies are inferred from the claim text.