Crosslinked double base propellant binders
AssigneeHercules Incorporated
InventorAnderson E. Robinson, Jr.
Life of this patent
Estimating the term…
Abstract
A crosslinked binder for crosslinked double base propellant is provided. The binder is prepared from nitrocellulose having a nitrogen content of 11 to 13.4% N and an intrinsic viscosity of 0.55 dl./gram to 2.0 dl./gram, a polymeric diol having a hydroxyl functionality of 1.9 to 2.1 and a polyfunctional isocyanate having an NCO functionality of at least three. The propellant prepared from the binder exhibits improved mechanical properties without detriment to ballistic performance.
Claims9
A crosslinked binder suitable as the binder portion of a crosslinked double base propellant composition in which the crosslinked binder is a urethane rubber comprising the reaction product of:
- (a) nitrocellulose having a nitrogen content of from about 11.0% to 13.4%, an intrinsic viscosity of at least about 0.55 dl./gram to about 2.0 dl./gram.;
- (b) a polymeric diol selected from the group consisting of polyester diols, polyether diols and polyester and polyether diols which have been chain extended by reaction with a diisocyanate, said polymeric diol having a hydroxyl functionality of from about 1.9 to about 2.1 and a molecular weight of from about 1,000 to 10,000;
- and
- (c) a polyfunctional isocyanate having an NCO functionality of at least three;
- in which the weight ratio of nitrocellulose to polymeric diol is from about 0.15 to about 0.001 and the ratio of isocyanate functional groups to the combined hydroxyl functionality of the nitrocellulose and polymeric diol is from about 1/1 to about 1.5/1.
In a crosslinked double base propellant composition comprising an energetic liquid nitrate ester plasticizer, nitrocellulose, organic and inorganic oxidizing agents, fuels, and a crosslinked binder, the improvement comprising as the crosslinked binder a urethane rubber comprising the reaction product of:
- (a) nitrocellulose having a nitrogen content of from about 11.0% to 13.4%, and an intrinsic viscosity of at least about 0.55 dl./gram to about 2.0 dl./gram.;
- (b) a polymeric diol selected from the group consisting of polyester diols, polyether diols and polyester and polyether diols which have been reacted with a diisocyanate, said polymeric diol having a hydroxyl functionality of from about 1.9 to about 2.1 and a molecular weight of from about 1,000 to 10,000;
- and
- (c) a polyisocyanate having an NCO functionality of at least three;
- in which the weight ratio of nitrocellulose to polymeric diol is from about 0.15 to about 0.001 and the ratio of isocyanate functional groups to the combined hydroxyl functionality of the nitrocellulose and polymeric diol is from about 1/1 to about 1.5/1 and in which the weight ratio of said plasticizer to binder is from about 2/1 to less than about 4.5/1.
A crosslinked double base propellant composition comprising by weight:
- (a) from about 15% to 25% by weight energetic liquid nitroester plasticizer;
- (b) from about 45% to 55% by weight or organic and inorganic oxidizing agents;
- (c) from about 18% to 22% by weight of particulate solid fuels;
- and;
- (d) from about 4% to 10% by weight of a urethane rubber binder, said binder comprising the reactionproduct of:
- (1) nitrocellulose having a nitrogen content of from about 11.0% to 13.4%, an intrinsic viscosity of at least about 0.55 dl./gram to about 2.0 dl./gram;
- (2) a polymeric diol selected from the group consisting of polyester diols, polyether diols and polyester and polyether diols which have been chain extended by reaction with a diisocyanate, said polymeric diol having a hydroxyl functionality of from about 1.9 to about 2.1 and a molecular weight of from about 1,000 to 10,000;
- and
- (3) a polyisocyanate having an NCO functionality of at least three;
- in which the weight ratio of nitrocellulose to polymeric diol is from about 0.15 to about 0.001 and the ratio of isocyanate functional groups to the combined hydroxyl functionality of the nitrocellulose and polymeric diol is from about 1/1 to about 1.5/1 and in which the weight ratio of said plasticizer to binder is from about 2/1 to less than about 4.5/1.
Dependencies are inferred from the claim text.