Automated catalyst processing for cloud electrode fabrication for fuel cells
AssigneeUnited Technologies Corporation
InventorsGlen J. Goller, Richard D. Breault
Life of this patent
Estimating the term…
Abstract
A process for making dry carbon/polytetrafluoroethylene floc material, particularly useful in the manufacture of fuel cell electrodes, comprises of the steps of floccing a co-suspension of carbon particles and polytetrafluoroethylene particles, filtering excess liquids from the co-suspension, molding pellet shapes from the remaining wet floc solids without using significant pressure during the molding, drying the wet floc pellet shapes within the mold at temperatures no greater than about 150.degree. F., and removing the dry pellets from the mold.
Claims11
The method of making an electrochemical cell catalyst material comprising the steps of:
- forming an aqueous co-suspension of polytetrafluoroethylene particles and catalyzed carbon to form a floc suspension;
- forming pellet shapes within a mold, the mold including a plurality of pellet shaped cavities with a porous filter medium forming the bottoms of the cavities, the step of forming pellet shapes including filling the mold cavities with the floc suspension and filtering out the excess liquids through the filter medium without the application of significant pressure leaving uncompressed wet floc solids within the mold cavities;
- drying the pellet shapes within the mold cavities at temperatures no greater than about 150.degree. F. for form dry, uncompressed floc pellets;
- and
- removing the pellets from the mold cavities.
In a method for applying a catalyst layer to the surface of electrochemical cell electrode substrates, the steps of:
- forming an aqueous co-suspension of catalyzed carbon particles and polytetrafluoroethylene particles;
- causing the carbon particles and polytetrafluoroethylene particles to floc and maintaining the floc in suspension;
- forming the floc into pellet shapes at essentially atmospheric pressure by pouring the suspension into a mold comprising a plurality of pellet shaped mold cavities with a porous filter medium forming the bottoms of the mold cavities, drawing a vacuum under the filter medium to draw excess liquid through the filter medium, wherein substantially uncompressed wet floc solids remain behind in the mold cavities;
- drying the pellet shapes within the mold cavities at temperatures no greater than about 120.degree. F. to form dry, uncompressed floc pellets;
- removing the dry floc pellets from the mold;
- placing the pellets in a hopper;
- automatically feeding, at spaced intervals, a predetermined amount of pellets from the hopper into grinding apparatus, the pre-determined amount of pellets being the amount necessary to apply a dry floc layer of certain catalyst loading to a single electrode substrate;
- grinding the predetermined amount of pellets in the grinding apparatus to form a powder having a maximum floc particle size of about 5 microns;
- applying the powder in dry form, as a uniform layer, directly from the grinding apparatus onto the surface of an electrochemical cell electrode substrate;
- compacting the layer;
- and
- sintering the layer.