US 4,231,993 AGranted

Recovery of metal values from lead smelter matte

AssigneeThe United States of America as represented by the Secretary of the Interior

InventorsRichard G. Sandberg, Terry L. Hebble

Life of this patent

Estimating the term…

Loading patent…

Abstract

A multi-step process for recovering metal values from lead smelter matte. The matte is mixed with sulfuric acid and manganese oxide and leaching is effected at atmospheric pressure to form an aqueous solution including dissolved metal sulfates and a residue containing sulfur and lead sulfate. The sulfur is removable by conventional means and the lead sulfate may be returned to the smelter. The pH of the aqueous sulfate solution is adjusted to 3.5 to 4.5 to precipitate ferric iron and arsenic and pH is readjusted to about 3.0 to redissolve coprecipitated copper. After separation from the precipitate, the aqueous solution is mixed with a sulfiding agent, such as sodium sulfide at a pH of not more than 3 to selectively precipitate copper sulfide. After separating the copper sulfide, the aqueous solution is mixed with further sulfiding agent at a pH of 3 to 4.5 to form a cobalt-nickel sulfide precipitate in which the weight ratio of copper-nickel to sulfur is 1.8. After separation of the precipitate, the pH of the solution is adjusted to 3 to 7 to form a manganese sulfate slurry. The slurry is reacted with oxygen at a temperature of 25.degree.-75.degree. C. to form a manganese-containing precipitate. The precipitate is separated from the brine and heated in a furnace to form manganese oxide which is recycled to the leaching step. The brine is also recycled to the leaching step as a source of sulfuric acid.

A method of recovering metal values from lead smelter matte containing cobalt, nickel, copper, iron and arsenic which comprises the steps of:

(a) mixing finely divided lead smelter matte, maganese (III) or manganese (IV) oxide and sulfuric acid to form an aqueous solution having a pH of not more than 3.5 and containing cobalt, nickel, copper, iron, arsenic and manganese sulfates and an insoluble solids residue containing sulfur and lead sulfate;
(b) separating the insoluble solids residue and the aqueous solution;
(c) adjusting the pH of the separated aqueous sulfate solution from step (b) to 3.5 to 4.5 to precipitate ferric iron and arsenic and further adjusting the pH of the solution to a pH of about 3.0 to redissolve coprecipitated copper;
(d) separating the precipitated ferric iron and arsenic from the aqueous solution;
(e) mixing the separated aqueous solution from step (d) with a sulfide precipitating agent at a pH of not more than 3 to selectively precipitate copper sulfide;
(f) separating the copper sulfide from the aqueous solution;
(g) mixing the aqueous solution separated by step (f) with a sulfiding agent at a pH of 3 to 4.5 to form a cobalt-nickel sulfide precipitate;
(h) separating the cobalt-nickel sulfide precipitate from the aqueous solution;
(i) adjusting the pH of the aqueous solution separated by step (h) to a pH of 3 to 7 by means of MgO, NaOH or Na.sub.2 CO.sub.3 to form a slurry containing manganese sulfate;
(j) reacting the slurry containing manganese sulfate with oxygen at a temperature of 25.degree. to 75.degree. C. to form a manganese-containing precipitate selected from the group consisting of manganese hydroxide and manganese carbonate;
(k) separating the manganese-containing precipitate from the aqueous solution;
(l) heating the manganese-containing precipitate of step (j) to produce manganese oxide;
(m) returning at least a portion of the separated aqueous solution of step (k) to step (a) to provide sulfuric acid for mixing with said lead smelter matte and said manganese oxide;
and
(n) returning at least a portion of the manganese oxide produced by step (l) to step (a) to provide manganese oxide for mixing with said sulfuric acid and said lead smelter matte.

12 more elements

Abstract

Claims20