Potting and encapsulating material for electronic circuits
AssigneeMotorola, Inc.
InventorsThomas A. Knappenberger, James F. Landers, Jr.
Life of this patent
Estimating the term…
Abstract
A homogeneous mixture of uncured thermosetting resin and curing agent in a flowable powder form with a particle size in the range of approximately 60 mesh to 200 mesh and curable in a range of approximately 125.degree. F. to 212.degree. F., and hollow microspheres having a diameter in the range of approximately 5 microns to 300 microns, with the resin-curing agent and microspheres being intermixed in a ratio in the range of approximately 35 percent to 45 percent resin-curing agent to microspheres by weight.
Claims9
Potting and encapsulating material for electronic circuits utilized in high acceleration and high thermal cycling environments consisting essentially of an intermixed compound of uncured thermosetting resin and curing agent in a flowable powder form with a particle size in the range of approximately 60 mesh to 200 mesh and curable in a range of approximately 125.degree. F. to 212.degree. F. at approximately ambient pressure, and hollow microspheres having a diameter in the range of approximately 5 microns to 300 microns said resin-curing agent and microspheres being intermixed in a ratio in the range of approximately 35 percent to 45 percent resin-curing agent to microspheres by weight.
Potting and encapsulating material for electronic circuits utilized in high acceleration and high thermal cycling environments consisting essentially of an intermixed compound of uncured thermosetting resin and curing agent in a flowable powder form with a particle size in the range of approximately 60 mesh to 200 mesh and curable in a range of approximately 125.degree. F. to 212.degree. F. at approximately ambient pressure, and hollow microspheres having a diameter in the range of approximately 5 microns to 300 microns, said resin-curing agent and microspheres being intermixed in a ratio such that the embedment stress of the cured material is under approximately 400 PSI at minus 30.degree. F. and is under approximately 10 PSI at the cure temperature.
Potting and encapsulating material for electronic circuits utilized in high acceleration and high thermal cycling environments consisting essentially of an intermixed compound of uncured thermosetting resin and curing agent in a flowable powder form with a particle size in the range of approximately 60 mesh to 200 mesh and curable in a range of approximately 125.degree. F. to 212.degree. F. at approximately ambient pressure, and hollow microspheres having a diameter in the range of approximately 5 microns to 300 microns, said resin-curing agent and microspheres being intermixed in a ratio such that the modulus of elasticity in compression is less than approximately 5000 PSI (5 PSI of stress for deflections in the range of 0 to 0.001 inches per inch of material).
A method of producing potting and encapsulating material having predetermined physical characteristics comprising the steps of:
- (a) selecting an uncured compound of theremosetting resin and curing agent in a flowable powder form with a particle size in the range of approximately 60 mesh to 200 mesh and curable in a temperature range of approximately 125.degree. F. to 212.degree. F. at approximately ambient pressure.
- (b) selecting a quantity of hollow microspheres having a diameter in the range of approximately 5 microns to 300 microns;
- and
- (c) mixing said compound and said microspheres into a substantially homogeneous mixture consisting essentially of said compound and said microspheres in a predetermined ratio in the range of approximately 35 percent to 45 percent resin-curing agent to microspheres by weight.
Dependencies are inferred from the claim text.