Fired iron-ore pellets having macro pores
AssigneeKobe Steel, Ltd.
InventorsIsao Fujita, Mamoru Onoda, Fumikazu Kawaguchi, Yoshimichi Takenake, Tadao Tsutaya
Life of this patent
Estimating the term…
Abstract
Fired iron-ore pellets are disclosed which are prepared by crushing iron ore to be pelletized, mixing a carbonaceous material of grain sizes ranging from 0.1 to 3 mm in diameter to the crushed iron ore in an amount of up to 4% by weight, pelletizing the mixture thus prepared, and firing the resulting pellets; thereby providing pellets throughout each of which is dispersed macro-pores of sizes ranging from 0.1 to 3 mm in diameter at a ratio of up to 25% relative to all pores contained in each pellet.
Claims1
Fired iron ore pellets containing macro pores ranging from 0.1 to 3 mm in diameter dispersed throughout each of said pellets at a ratio of from 5 to 25% relative to all of the pores contained in each pellet and which have been prepared by firing a green pellet comprising up to 4% of a carbonaceous material having a grain size of from 0.1 to 3 mm, from 3 to 9% dolomite, iron ore particles wherein 60-95% of the said iron particles are up to 44.mu. in size and 15 to 25% of said iron ore particles are up to 10.mu. in size, and limestone in an amount so as to adjust the CaO/SiO.sub.2 ratio to about 1.2.
Dependencies are inferred from the claim text.