Process for the preparation of tantalum and niobium powders of improved efficiency
AssigneeHermann C. Starck Berlin
InventorsReinhard Hahn, Dieter Behrens
Life of this patent
Estimating the term…
Abstract
An anhydrous mixture of extrudable viscosity of an activated alkali metal tantalum or niobium halide powder, an alkali metal halide powder, and a molten alkali metal in about 1:0.75-2.0:4.75-5.5 molar ratio is formed into a paste which is extruded and formed into masses of critical dimensions and temperature. The mass is ignited and a self-sustaining reduction reaction ensues. The reaction product is powdered, washed and dried. The product is pure tantalum or niobium powder in almost quantitative yield. The powder is specially suited for use as electrolytic capacitor anodes. The powder is improved by passage through a plasma of an inert gas. The process can be performed on a continuous scale.
Claims21
A process for the preparation of a powder of high electrical capacitance of a transition metal of atomic number above 23 of column d3 of the Periodic Chart of Elements, which comprises the steps of:
- heating a shallow bed of a powdered alkali metal transition metal halide selected from the group consisting of alkali metal tantalum halide and alkali metal niobium halide in a vacuum and/or under an inert atmosphere thereby removing any water and hydrogen halide present at a temperature of about 325.degree. C. up to the sintering point of said powder to such an extent that said heating decrepitates said alkali metal transition metal halide;
- mixing said powder maintained under a dry inert gas with powdered anhydrous alkali metal halide maintained under a dry inert gas and alkali metal maintained under a dry inert gas in 1:0.75-2.0:4.75-5.5 molar ratio at a temperature above the liquefaction point of said metal and below the ignition point of said mixture thereby forming a paste;
- forming said paste into shaped masses;
- cooling said shaped masses to a temperature below 50.degree. C. and then igniting said shaped masses by contacting said shaped masses at a single point with a glowing external ignitor thereby initiating a reduction reaction and forming elementary tantalum or niobium;
- allowing said reaction to go to substantial completion in the absence of external application of heat;
- the dimensions of said shaped masses and their temperature at ignition of below 50.degree. C. being predetermined so that the maximum temperature reached by said shaped masses during said reaction is less than about 800.degree. C. and is between about three and five times the ignition temperature of the paste;
- cooling said reacted shaped masses;
- and pulverizing the reaction product and removing any alkali metal halide and alkali metal present;
- said steps being performed in an inert atmosphere or under vacuum while any alkali metal is present.
A continuous process for the manufacture of tantalum metal powder which comprises heating a shallow bed of a powdered alkali metal tantalum halide in a vacuum and/or under an inert atmosphere thereby removing any water and hydrogen halide present at a temperature of about 325.degree. C. up to the sintering point of said powder to such an extent that said heating decrepitates said alkali metal tantalum halide, mixing said powder maintained under a dry inert gas with dry powdered anhydrous alkali metal halide maintained under a dry inert gas and an alkali metal maintained under a dry inert gas in 1:0.75-2.0:4.75-5.5 molar ratio at a temperature above the melting point of said metal and below the ignition point of said mixture thereby forming an extrudable paste, extruding said paste into shaped masses in open containers, the dimension of said shaped masses of paste in said open containers and their temperature at ignition of below 50.degree. C. being predetermined so that the maximum temperature reached by said shaped masses during said reaction is less than about 800.degree. C. and is between about three and five times the ignition temperature of the paste, conveying said shaped masses in open containers therefor through a continuous reaction chamber having an inert atmosphere and a cooling section, an ignition section, a combustion section and another cooling section, cooling said shaped masses in said containers in said cooling section to a temperature below 50.degree. C., igniting said shaped masses in said container in said ignition section by contacting said shaped masses at a single point with a glowing external ignitor, allowing the combustion which occurs to proceed to completion in said combustion section in the absence of external application of heat, cooling said reacted shaped masses in said cooling section to below 50.degree. C., discharging said containers from said reaction chamber, removing the reaction product from said containers, recycling said containers, and removing any alkali metal halide and alkali metal present in said reaction product, said reaction mixture being maintained under an inert atmosphere at least until said reaction is substantially complete.
Dependencies are inferred from the claim text.