Process for purifying solid substances
AssigneeWacker-Chemitronic Gesellschaft fur Elektronik-Grundstoffe mbH
InventorsHeinz Herzer, Heinz-Jorg Rath, Dietrich Schmidt
Life of this patent
Estimating the term…
Abstract
A process for purifying solid substances by melting and subsequent resoliication, wherein a melted bath of the solid substance is formed, a roller is placed in the bath so that a first portion of its surface is in contact with the melted substance, and the surface of the roller is cooled to a temperature below the melting point of the solid substance. The cooled roller is rotated in the melted substance to collect a solidified film of the substance on the roller surface. A second portion of the roller surface is passed through a heated zone at a temperature above the melting point of the solid substance, so that the solidified film is remelted and collected in an appliance.
Claims5
In a process for purifying semiconductor silicon by melting and subsequent resolidification, the improvement comprising the steps of:
- forming a melted bath of the silicon to be purified at a temperature between 1430.degree. and 1500.degree. C.;
- disposing a roller in the bath to a depth of between 0.01 to 0.3 times the diameter of the roller;
- cooling the roller internally to a temperature between 800.degree. and 1200.degree. C.;
- rotating the cooled roller in the melted silicon to form a solidified silicon film, wherein the residence time of the roller surface in the melted silicon, measured in minutes, is 0.0025 to 0.5 times the numerical value for the roller diameter;
- remelting the silicon film formed on said roller at a distance of 0.1 to 0.5 d. .pi. from the surface of the melt, measured on the circumference of the roller, wherein d. is the diameter of the roller;
- and
- collecting the remelted silicon in an appliance.
In a process for purifying semiconductor silicon by melting and subsequent resolidification, wherein the purifying action of the process is dependent upon the segregation coefficients of the impurities, the improvement comprising the steps of:
- forming a melted bath of the silicon to be purified at a temperature between 1430.degree. and 1500.degree. C.;
- disposing a roller in the bath to a depth of between 0.01 to 0.3 times the diameter of the roller;
- cooling the roller internally to a temperature between 800.degree. and 1200.degree. C.;
- rotating the cooled roller in the melted silicon to form a solidified silicon film, wherein the residence time of the roller surface in the melted silicon, measured in minutes, is 0.0025 to 0.5 times the numerical value for the roller diameter, said silicon film containing substantially less impurities than the melted bath from which it was formed due to the segregation coefficients of the impurities contained therein;
- remelting the silicon film formed on said roller at a distance of 0.1 to 0.5 d. .pi. from the surface of the melt, measured on the circumference of the roller, wherein d. is the diameter of the roller;
- collecting the remelted purified silicon in an appliance;
- and
- casting said purified silicon into plates for the production of solar cells.
Dependencies are inferred from the claim text.