Cold-water dispersible, gelling starch
AssigneeNational Starch and Chemical Corporation
InventorsChung W. Chiu, Morton W. Rutenberg
Life of this patent
Estimating the term…
Abstract
A cold-water dispersible, modified starch characterized by forming a gel having a Bloom strength of at least 50 grams is prepared by reacting a tapioca starch with a crosslinking agent to within defined Brabender viscosity limits; converting the crosslinked starch in a sufficient amount to provide the modified starch with gelling properties; and drum-drying the crosslinked and converted starch to obtain the modified starch product. The gelling instant starch thus prepared is particularly useful in food systems of the type which gel upon standing, such as pie filling, jellies, and puddings.
Claims9
A cold-water dispersible, modified tapioca starch with gelling properties, prepared by drum-drying a tapioca starch which has been reacted with a crosslinking agent such that the crosslinked starch has a peak Brabender viscosity of from about 250 to about 850 B.U. and reaches peak viscosity from 50.degree. C. in about 22 to 65 minutes, the crosslinked starch being thereafter converted such that the crosslinked, converted starch has a Brabender Viscosity Differential, measured between 80.degree. and 95.degree. C., of from about -40 to about +55% and has a minimum Brabender viscosity at 80.degree. C. of about 100 B.U., said starch after drum drying being capable of forming a gel having a Bloom strength of at least 50 grams.
A process for preparing a cold-water dispersible, modified tapioca starch with gelling properties comprising the steps of:
- a. reacting a tapioca starch with a crosslinking agent such that the crosslinked starch has a peak Brabender viscosity of from about 250 to about 850 B.U. and reaches peak viscosity from 50.degree. C. in about 22 to 65 minutes;
- b. converting the crosslinked starch such that the crosslinked, converted starch has a Brabender Viscosity Differential, measured between 80.degree. and 95.degree. C., of from about -40 to about +55% and has a minimum Brabender viscosity at 80.degree. C. of about 100 B.U.;
- and
- c. drum-drying the crosslinked, converted starch to obtain said modified starch, said modified starch being defined as capable of forming a gel having a Bloom strength of at least 50 grams.